PP Fiberfil® J-60/15/UV/HS Canada Fiberfil
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | Canada Fiberfil/Fiberfil® J-60/15/UV/HS |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 100-110 R |
| Mechanical properties | Test Condition | Test Method | Canada Fiberfil/Fiberfil® J-60/15/UV/HS |
|---|---|---|---|
| bending strength | 23°C | ASTM D790 | 65.0 MPa |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 42.7 J/m |
| 屈服伸长率 | ASTM D638 | 3.5 % | |
| Tensile modulus | 23°C | ASTM D638 | 2760 MPa |
| Flexural modulus | 23°C | ASTM D790 | 2600 MPa |
| tensile strength | 屈服,23°C | ASTM D638 | 62.1 MPa |
| physical property | Test Condition | Test Method | Canada Fiberfil/Fiberfil® J-60/15/UV/HS |
|---|---|---|---|
| melt mass-flow rate | 收缩率 | ASTM D995 | 0.60 % |
| Shrinkage rate | TD,3.17mm | ASTM D995 | 0.50 % |
| Water absorption rate | (23°C,24hr) | ASTM D570 | 0.030 % |
| density | ASTM D792 | 1.00 g/cm³ | |
| melt mass-flow rate | ℃/Kg | ASTM D1238 | 8.0 g/10min |
| Shrinkage rate | MD,3.17mm | ASTM D995 | 0.40 % |
| Thermal performance | Test Condition | Test Method | Canada Fiberfil/Fiberfil® J-60/15/UV/HS |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa未退火，HDT | ASTM D648 | 138 °C |
| 0.45MPa未退火，HDT | ASTM D648 | 149 °C |