Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
LDPE LD5320 HANWHA KOREA
--
chip、film
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | HANWHA KOREA/LD5320 |
|---|---|---|---|
| elongation | TD:断裂,50µm | ASTM D882 | 620 % |
| tensile strength | TD:断裂,50µm | ASTM D882 | 17.2 Mpa |
| Tensile tear strength | TD:50.0µm | Kg/m | 98.1 kN/m |
| film thickness | 50 µm | ||
| Dart impact | 50µm | ASTM D1709 | 95 g |
| elongation | MD:断裂,50µm | ASTM D882 | 310 % |
| tensile strength | MD:断裂,50µm | ASTM D882 | 22.6 Mpa |
| Tensile tear strength | MD:50.0µm | Kg/m | 107.9 kN/m |
| Mechanical properties | Test Condition | Test Method | HANWHA KOREA/LD5320 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 750 % |
| tensile strength | 断裂 | ASTM D638 | 13.7 Mpa |
| optical performance | Test Condition | Test Method | HANWHA KOREA/LD5320 |
|---|---|---|---|
| Haze ratio | 50.0µm | ASTM D1003 | 8.5 % |
| physical property | Test Condition | Test Method | HANWHA KOREA/LD5320 |
|---|---|---|---|
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 2.0 g/10min |
| Thermal performance | Test Condition | Test Method | HANWHA KOREA/LD5320 |
|---|---|---|---|
| vicat | ASTM D1525 | 90.0 °C | |
| melting temperature | 内部方法 | 110 °C | |
| brittle temperature | ASTM D746 | <-76.0 °C |