EVOH C109B KURARAY JAPAN
EVAL™
--
Lubricity、copolymer
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | KURARAY JAPAN/C109B |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2500 Mpa | |
| Charpy Notched Impact Strength | ISO 179 | 1.0 kJ/m² | |
| Tensile strain | 断裂 | ISO 527-2 | 6.0 % |
| Flexural modulus | ISO 178 | 4800 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 68.0 Mpa |
| Rockwell hardness | M 计秤 | ISO 2039-2 | 94 |
| physical property | Test Condition | Test Method | KURARAY JAPAN/C109B |
|---|---|---|---|
| melt mass-flow rate | 190℃/2.16 kg | ISO 1133 | 9.3 g/10 min |
| Ethylene component | 35.0 wt% | ||
| melt mass-flow rate | 210℃/2.16 kg | ISO 1133 | 21 g/10 min |
| Thermal performance | Test Condition | Test Method | KURARAY JAPAN/C109B |
|---|---|---|---|
| Glass Transition Temperature | DSC | DSC | 53.0 °C |
| Crystallization peak temperature | DSC | ISO 3146 | 154 °C |
| melting temperature | ISO 3146 | 177 °C |