PC TEIJIN JAPAN G-3420R

Injection grade

US$ 3,570 / MT

FOB Shenzhen Port

flammability	Test Condition	Test Method	TEIJIN JAPAN/G-3420R
UL flame retardant rating	0.8mm	UL 94	V-2
		3.0mm	UL 94	V-1
		0.43mm	UL 94	HB
mechanical properties	Test Condition	Test Method	TEIJIN JAPAN/G-3420R
bending strength		ISO 178	140 Mpa
Tensile strain	Break	ISO 527-2/5	2.5 %
Charpy Notched Impact Strength		ASTM D256/ISO 179	137(14) kg·cm/cm(J/M)ft·lb/in
Tensile modulus		ISO 527-2/1	6100 Mpa
bending strength		ASTM D790/ISO 178	157(1600) kg/cm²(MPa)[Lb/in²]
tensile strength	Break	ISO 527-2/5	90.0 Mpa
Tensile modulus		ASTM D638/ISO 527	5890(60000) kg/cm²(MPa)[Lb/in²]
Elongation at Break		ASTM D638/ISO 527	4.5 %
Bending modulus		ISO 178	5400 Mpa
tensile strength		ASTM D638/ISO 527	105(1070) kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	5400(55000) kg/cm²(MPa)[Lb/in²]
Physical properties	Test Condition	Test Method	TEIJIN JAPAN/G-3420R
Water absorption rate		ASTM D570/ISO 62	0.14 %
Shrinkage rate	MD:4.00mm	Internal Method	0.10-0.30 %
Water absorption rate	23°C,24hr	ISO 62	0.14 %
Shrinkage rate	TD:4.00mm	Internal Method	0.40-0.60 %
density		ASTM D792/ISO 1183	1.34
other	Test Condition	Test Method	TEIJIN JAPAN/G-3420R
characteristic			标准规格型
thermal performance	Test Condition	Test Method	TEIJIN JAPAN/G-3420R
Linear coefficient of thermal expansion	MD	ISO 11359-2	3E-05 cm/cm/°C
RTI Str	1.5mm	UL 746	130 °C
RTI Imp	1.5mm	UL 746	125 °C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	150 °C
Linear coefficient of thermal expansion	TD	ISO 11359-2	6E-05 cm/cm/°C
RTI Elec	1.5mm	UL 746	130 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	147 °C
Vicat softening temperature		ISO 306/B50	152 °C
Electrical performance	Test Condition	Test Method	TEIJIN JAPAN/G-3420R
Dissipation factor	100Hz	IEC 60250	1E-03
Compared to the anti leakage trace index		IEC 60112	PLC 3
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm
Dissipation factor	1MHz	IEC 60250	9E-03
Relative permittivity	100Hz	IEC 60250	3.40
Surface resistivity		IEC 60093	>1.0E+15 ohms
Relative permittivity	1MHz	IEC 60250	3.40
Dielectric strength		IEC 60243-1	35 KV/mm
impact performance	Test Condition	Test Method	TEIJIN JAPAN/G-3420R
Impact strength of simply supported beam without notch		ISO 179	40 kJ/m²