PBT 1101G-15 TORAY JAPAN
Toraycon®
Automotive sector,Electronic field,Electrical field
Glass fiber reinforced,Flame retardant,High impact resistance,Filler: Glass fiber reinf,15% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Mechanical properties | Test Condition | Test Method | TORAY JAPAN/1101G-15 |
---|---|---|---|
elongation | 23℃ | ASTM D638 | 4 % |
Tensile strain | 断裂,23°C | ISO 527-2 | 2.7 % |
Rockwell hardness | ASTM D785 | 90 M | |
tensile strength | 屈服,23°C | ISO 527-2 | 97.0 Mpa |
23℃ | ASTM D638 | 120 Mpa | |
bending strength | 23℃ | ASTM D790 | 175 Mpa |
Flexural modulus | 23℃ | ASTM D790 | 7.6 GPa |
Impact strength of cantilever beam gap | 缺口,23℃ | ASTM D256 | 186 J/m |
缺口,-40℃ | ASTM D256 | 135 J/m | |
coefficient of friction | 对金属 | ASTM D1894 | 0.17 |
对本身 | ASTM D1894 | 0.20 | |
Impact strength of cantilever beam gap | 无缺口,23℃ | ASTM D256 | 60 KJ/m |
Electrical performance | Test Condition | Test Method | TORAY JAPAN/1101G-15 |
---|---|---|---|
arc resistance | ASTM D495 | 131 S | |
dielectric constant | 50Hz | ASTM D150 | 3.8 |
Dielectric loss | 10,正切 | ASTM D150 | 0.02 |
dielectric strength | ASTM D149 | 28 MV/m | |
dielectric constant | 10 | ASTM D150 | 3.7 |
Dielectric loss | 50Hz,正切 | ASTM D150 | 0.002 |
Volume resistivity | ASTM D257 | 7.0 |
flammability | Test Condition | Test Method | TORAY JAPAN/1101G-15 |
---|---|---|---|
UL flame retardant rating | UL 94 | HB |
physical property | Test Condition | Test Method | TORAY JAPAN/1101G-15 |
---|---|---|---|
Water absorption rate | 23℃,24hr | ASTM D570 | 0.07 % |
Thermal performance | Test Condition | Test Method | TORAY JAPAN/1101G-15 |
---|---|---|---|
Heat distortion temperature | 0.45MPa,HDT | ASTM D648 | 220 °C |
Linear coefficient of thermal expansion | ASTM D696 | 2.5 | |
Heat distortion temperature | 1.82Mpa,HDT | ASTM D648 | 210 °C |
UL flame retardant rating | UL 94 | HB |