Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC BPL1000-7P20070 SABIC INNOVATIVE CHONGQING
LEXAN™
Automotive components、Electronic and electrical、Thin walled products
UV resistance、Hydrolysis resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE CHONGQING/BPL1000-7P20070 |
|---|---|---|---|
| CharpyNotchedImpactStrength8 | 23°C | ISO179/1eA | 18 kJ/m² |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 48.6 J |
| Suspended wall beam gap impact strength 9 | 23°C | ISO180/1A | 18 kJ/m² |
| -30°C | ISO180/1A | 12 kJ/m² |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE CHONGQING/BPL1000-7P20070 |
|---|---|---|---|
| Surface Resistivity | IEC60093 | >1.0E+15 ohms | |
| 50Hz | IEC60250 | 3.00 | |
| CTI | IEC60112 | 200 V | |
| dielectric strength | 1.60mm,inOil | ASTMD149 | 27 KV/mm |
| Volume resistivity | IEC60093 | >1.0E+15 ohms·cm | |
| Dissipation Factor | 60Hz | IEC60250 | 0.030 |
| 50Hz | IEC60250 | 0.030 | |
| 1MHz | IEC60250 | 0.010 | |
| 60Hz | IEC60250 | 3.00 | |
| 1MHz | IEC60250 | 2.90 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE CHONGQING/BPL1000-7P20070 |
|---|---|---|---|
| Tensile stress | 屈服 | ISO527-2/50 | 64.8 Mpa |
| elongation | 断裂 | ASTMD638 | 96 % |
| Bending modulus 6 | ISO178 | 2370 Mpa | |
| Tensile strength 4 | Break | ASTMD638 | 51.0 Mpa |
| Flexural Strength5 | Yield,50.0mmSpan | ASTMD790 | 102 Mpa |
| Tensile strain | 屈服 | ISO527-2/50 | 4.7 % |
| Tensile modulus 3 | ASTMD638 | 2680 Mpa | |
| Tensile stress | 断裂 | ISO527-2/50 | 53.5 Mpa |
| elongation | 屈服 | ASTMD638 | 4.8 % |
| Tensile modulus | ISO527-2/1 | 2460 Mpa | |
| Bending strength 6,7 | ISO178 | 94.8 Mpa | |
| Tensile strain | 断裂 | ISO527-2/50 | 97 % |
| Flexural modulus | 50.0mmSpan | ASTMD790 | 2670 Mpa |
| Tensile strength 4 | 屈服 | ASTMD638 | 63.4 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE CHONGQING/BPL1000-7P20070 |
|---|---|---|---|
| Burning wire flammability index | 1.0mm | IEC60695-2-12 | 960 °C |
| UL flame retardant rating | 0.45mm | UL94 | V-2 |
| Hot filament ignition temperature | 1.0mm | IEC60695-2-13 | 800 °C |
| UL flame retardant rating | 0.8mm | UL94 | V-0 |
| Limiting Oxygen Index | ISO4589-2 | 36 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE CHONGQING/BPL1000-7P20070 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.70 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 0.15 % |
| 饱和,23°C | ISO62 | 0.35 % | |
| melt mass-flow rate | 300°C/1.2kg | ASTMD1238 | 25 g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 23.2 cm3/10min |
| Shrinkage rate | TD：3.20mm | 内部方法 | 0.50to0.70 % |
| MD：--2 | 内部方法 | 0.50to0.70 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE CHONGQING/BPL1000-7P20070 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 106 °C |
| Hot deformation temperature 10 | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 96.1 °C |
| MD：-40到40°C | ISO11359-2 | 7E-05 cm/cm/°C | |
| TD：-40到40°C | ISO11359-2 | 7E-05 cm/cm/°C | |
| vicat | -- | ISO306/B50 | 113 °C |
| RTI Imp | UL746 | 80.0 °C | |
| RTI Str | UL746 | 80.0 °C | |
| BallPressure Test | 75°C | IEC60695-10-2 | Pass |
| MD：-40到40°C | ASTME831 | 7E-05 cm/cm/°C | |
| RTI Elec | UL746 | 80.0 °C | |
| vicat | ASTMD152511 | 111 °C | |
| -- | ISO306/B120 | 114 °C | |
| TD：-40到40°C | ASTME831 | 7E-05 cm/cm/°C |