Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM WR90Z CELANESE USA
CELCON®
Automotive Applications,pipeline,Outdoor applications,currency,Application in the automotive field
copolymer,UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | CELANESE USA/WR90Z |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 5.5 kJ/m² |
| -30°C | ISO 179/1eA | 5.5 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 99 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 5.5 kJ/m² |
| Mechanical properties | Test Condition | Test Method | CELANESE USA/WR90Z |
|---|---|---|---|
| Tensile strain | 屈服 | ISO 527-2/1A/50 | 8.0 % |
| Tensile modulus | ISO 527-2/1A/1 | 2650 Mpa | |
| Flexural modulus | 23°C | ISO 178 | 2550 Mpa |
| tensile strength | 屈服,23°C | ASTM D638 | 60.7 Mpa |
| 屈服 | ISO 527-2/1A/50 | 63.0 Mpa |
| physical property | Test Condition | Test Method | CELANESE USA/WR90Z |
|---|---|---|---|
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 8.00 cm3/10min |
| Shrinkage rate | MD | ASTM D955 | 2.2 % |
| TD | ISO 294-4 | 1.6 % | |
| MD | ISO 294-4 | 1.7 % | |
| density | ASTM D792 | 1.41 g/cm³ | |
| Shrinkage rate | TD | ASTM D955 | 1.8 % |
| density | ISO 1183 | 1.41 g/cm³ | |
| melt mass-flow rate | ASTM D1238 | 9.0 g/10min |
| Thermal performance | Test Condition | Test Method | CELANESE USA/WR90Z |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 110 °C |
| melting temperature | ISO 11357-3 | 166 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 152 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 95.0 °C | |
| melting temperature | ASTM D3418 | 165 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1E-04 cm/cm/°C |
| TD | ISO 11359-2 | 1.1E-04 cm/cm/°C |