PP Copolymer WINTEC™ WMG03UX Japan Polychem Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Japan Polychem Corporation/WINTEC™ WMG03UX |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 3.3 kJ/m² |
| hardness | Test Condition | Test Method | Japan Polychem Corporation/WINTEC™ WMG03UX |
|---|---|---|---|
| Rockwell hardness | R计秤 | ISO 2039-2 | 95 |
| Mechanical properties | Test Condition | Test Method | Japan Polychem Corporation/WINTEC™ WMG03UX |
|---|---|---|---|
| Flexural modulus | ISO 178 | 1450 MPa |
| optical performance | Test Condition | Test Method | Japan Polychem Corporation/WINTEC™ WMG03UX |
|---|---|---|---|
| gloss | ASTM D523 | 110 | |
| Haze ratio | 1000µm | ISO 14782 | 3.0 % |
| 2000µm | ISO 14782 | 10 % |
| physical property | Test Condition | Test Method | Japan Polychem Corporation/WINTEC™ WMG03UX |
|---|---|---|---|
| melt mass-flow rate | ISO 1133 | 30 g/10min | |
| Shrinkage rate | 内部方法 | 1.4to1.6 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | <0.030 % |
| density | ISO 1183 | 0.900 g/cm³ |
| Thermal performance | Test Condition | Test Method | Japan Polychem Corporation/WINTEC™ WMG03UX |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 90.0 °C |