Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT GP-2306F LG GUANGZHOU
LUPOX®
Electronic field,Electrical field,Electrical components,Electrical/Electronic Applications
Flame retardant,Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LG GUANGZHOU/GP-2306F |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,6.40mm | ASTM D256 | 69 J/m |
| thermal performance | Test Condition | Test Method | LG GUANGZHOU/GP-2306F |
|---|---|---|---|
| RTI Elec | UL 746 | 140 °C | |
| RTI Imp | UL 746 | 140 °C | |
| melting temperature | ASTM D3418 | 223 °C | |
| RTI | UL 746 | 140 °C | |
| Heat Deflection Temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 210 °C |
| Electrical performance | Test Condition | Test Method | LG GUANGZHOU/GP-2306F |
|---|---|---|---|
| arc resistance | ASTM D495 | PLC6 | |
| volume resistivity | ASTM D257 | 1E+17 ohms·cm | |
| dielectric strength | 1.00mm | ASTM D149 | 28 KV/mm |
| Mechanical properties | Test Condition | Test Method | LG GUANGZHOU/GP-2306F |
|---|---|---|---|
| flexural modulus | 3.20mm | ASTM D790 | 8830 Mpa |
| tensile strength | 断裂,3.20mm | ASTM D638 | 132 Mpa |
| elongation | 断裂,3.20mm | ASTM D638 | 2.0 % |
| bending strength | 屈服,3.20mm | ASTM D790 | 191 Mpa |
| Physical properties | Test Condition | Test Method | LG GUANGZHOU/GP-2306F |
|---|---|---|---|
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.070 % |
| shrinkage rate | MD | ASTM D955 | 0.30-1.0 % |
| density | ASTM D792 | 1.62 g/cm³ | |
| melt mass-flow rate | 250°C/2.16kg | ASTM D1238 | 10 g/10min |
| flammability | Test Condition | Test Method | LG GUANGZHOU/GP-2306F |
|---|---|---|---|
| UL flame retardant rating | 3.3mm | UL 94 | V-0 |
| 1.5mm | UL 94 | V-0 | |
| 0.71mm | UL 94 | V-0 |