Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS Abstron KU602L Bhansali Engineering Polymers Limited
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Bhansali Engineering Polymers Limited/Abstron KU602L |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,6.40mm,注塑 | ASTM D256 | 200 J/m |
| 23°C,3.20mm,注塑 | ASTM D256 | 240 J/m |
| hardness | Test Condition | Test Method | Bhansali Engineering Polymers Limited/Abstron KU602L |
|---|---|---|---|
| Rockwell hardness | R级,注塑 | ASTM D785 | 103 |
| Mechanical properties | Test Condition | Test Method | Bhansali Engineering Polymers Limited/Abstron KU602L |
|---|---|---|---|
| Flexural modulus | 6.40mm,注塑 | ASTM D790 | 2160 MPa |
| bending strength | 屈服,6.40mm,注塑 | ASTM D790 | 68.6 MPa |
| tensile strength | 屈服,3.20mm,注塑2 | ASTM D638 | 46.1 MPa |
| 屈服,3.20mm,注塑3 | ASTM D638 | 50.0 MPa |
| flammability | Test Condition | Test Method | Bhansali Engineering Polymers Limited/Abstron KU602L |
|---|---|---|---|
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| physical property | Test Condition | Test Method | Bhansali Engineering Polymers Limited/Abstron KU602L |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.30to0.50 % |
| density | ASTM D792 | 1.05 g/cm³ | |
| melt mass-flow rate | 220°C/10.0kg | ASTM D1238 | 5.0 g/10min |
| Thermal performance | Test Condition | Test Method | Bhansali Engineering Polymers Limited/Abstron KU602L |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,退火,6.40mm,注塑，HDT | ASTM D648A | 105 °C |