PP Copolymer WPP PP PPC3TF2-Black Washington Penn Plastic Co. Inc.
--
Automotive internal equipment and applications in the automotive field
Filler, Washington, Penn, Washington, USA, Penn
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | Washington Penn Plastic Co. Inc./WPP PP PPC3TF2-Black |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179 | 3.0 kJ/m² |
Impact strength of cantilever beam gap | 23°C | ASTM D256 | 41 J/m |
23°C | ISO 180 | 4.0 kJ/m² | |
10°C | ISO 180 | 3.5 kJ/m² | |
-40°C | ISO 180 | 2.0 kJ/m² |
hardness | Test Condition | Test Method | Washington Penn Plastic Co. Inc./WPP PP PPC3TF2-Black |
---|---|---|---|
Shore hardness | 邵氏D,15秒 | ISO 868 | 66 |
Mechanical properties | Test Condition | Test Method | Washington Penn Plastic Co. Inc./WPP PP PPC3TF2-Black |
---|---|---|---|
Flexural modulus | ASTM D790 | 2100 MPa | |
tensile strength | 屈服 | ASTM D638 | 28.0 MPa |
Flexural modulus | ISO 178 | 2200 MPa | |
tensile strength | 屈服 | ISO 527-2/50 | 29.0 MPa |
physical property | Test Condition | Test Method | Washington Penn Plastic Co. Inc./WPP PP PPC3TF2-Black |
---|---|---|---|
melt mass-flow rate | 230°C/2.16kg | ASTM D1238 | 12 g/10min |
density | ASTM D792 | 1.06 g/cm³ | |
ISO 1183 | 1.06 g/cm³ | ||
melt mass-flow rate | 230°C/2.16kg | ISO 1133 | 12 g/10min |
Thermal performance | Test Condition | Test Method | Washington Penn Plastic Co. Inc./WPP PP PPC3TF2-Black |
---|---|---|---|
Heat distortion temperature | 1.8MPa,未退火,HDT | ASTM D648 | 66.0 °C |
1.8MPa,未退火,HDT | ISO 75-2/Af | 66.0 °C | |
0.45MPa,未退火,HDT | ISO 75-2/B | 116 °C | |
1.8MPa,未退火,HDT | ISO 75-2/A | 68.0 °C |