PC ML-3104ZLP TEIJIN JAPAN
PANLITE®
Casters
standard、High temperature resistan、Flame retardant、optical performance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | TEIJIN JAPAN/ML-3104ZLP |
|---|---|---|---|
| Heat Deflection Temperature | 线膨胀系数，MD | ISO 11359-2 | 0.7 X10-4/℃ |
| TD | 0.7 X10-4/℃ | ||
| Flame retardancy | 1.0mm/3.0mm | UL94 | V-2 |
| Heat Deflection Temperature | 1.80MPa | ISO 75-1,2 | 129 °C |
| Physical | Test Condition | Test Method | TEIJIN JAPAN/ML-3104ZLP |
|---|---|---|---|
| Modeling Shrinkage | MD | In-house method | 0.5-0.7 % |
| TD | 0.5-0.7 % | ||
| Melt Mass-Flow Rate | 300℃ | ISO 1133 | 18 cm310min |
| Mechanical Properties | Test Condition | Test Method | TEIJIN JAPAN/ML-3104ZLP |
|---|---|---|---|
| Notched Impact Strength | Notched | ISO 179 | 15 kJ/m² |
| Flexural Strength | 2mm/min | ISO 178 | 99 Mpa |
| Tensile Elongation?(Break) | 50mm/min | ISO 527-1 | 105 % |
| Tensile Strength(Yield) | ISO 527-1,2 | 61 Mpa | |
| Tensile Strength(Break) | ISO 527-1 | 68 Mpa | |
| Flexural Modulus | 2mm/min | ISO 178 | 2400 Mpa |
| Optical | Test Condition | Test Method | TEIJIN JAPAN/ML-3104ZLP |
|---|---|---|---|
| Particle Size Distribution | 2.0mmt | In-house method | 45 % |
| Transmittance | 1.5mmt | JIS K7136 | 63 % |