PC GS2010MKR PC vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Reference Price

PC MITSUBISHI ENGINEERING JAPAN GS2010MKR

Injection grade

US$ 2,800 / MT

FOB Shenzhen Port

machinability	Test Condition	Test Method	MITSUBISHI ENGINEERING JAPAN/GS2010MKR
Dry conditions			热风干燥 120℃---約4-8小时
Mold temperature			80-120 °C
Processing temperature			280-300 °C
Screw speed			50-100 rpm
mechanical properties	Test Condition	Test Method	MITSUBISHI ENGINEERING JAPAN/GS2010MKR
bending strength		ISO 178	135 Mpa
Tensile strain	Break	ISO 527-2	2.9 %
tensile strength	Break	ISO 527-2	78.0 Mpa
Tensile modulus		ISO 527-2	4500 Mpa
bending strength		ASTM D790/ISO 178	120 kg/cm²(MPa)[Lb/in²]
Tensile modulus		ASTM D638/ISO 527	4200 kg/cm²(MPa)[Lb/in²]
Elongation at Break		ASTM D638/ISO 527	3.4 %
Bending modulus		ISO 178	4000 Mpa
Bending modulus			ASTM D790/ISO 178	3500 kg/cm²(MPa)[Lb/in²]
flammability	Test Condition	Test Method	MITSUBISHI ENGINEERING JAPAN/GS2010MKR
UL flame retardant rating	0.75mm	UL 94	V-0
Physical properties	Test Condition	Test Method	MITSUBISHI ENGINEERING JAPAN/GS2010MKR
Shrinkage rate	MD:3.20mm		0.30-0.50 %
Shrinkage rate			ASTM D955	0.3 - 0.5 %
melt mass-flow rate	300°C/1.2kg	ISO 1133	10 g/10min
Shrinkage rate	TD:3.20mm		0.40-0.60 %
Water absorption rate	Saturation,23°C	ISO 62	0.14 %
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	9.00 cm3/10min
density		ASTM D792/ISO 1183	1.27
thermal performance	Test Condition	Test Method	MITSUBISHI ENGINEERING JAPAN/GS2010MKR
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	4.0E-05 mm/mm.℃
Linear coefficient of thermal expansion		MD	ISO 11359-2	4E-05 cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	145 °C
Linear coefficient of thermal expansion	TD	ISO 11359-2	6.7E-05 cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	140 °C
Electrical performance	Test Condition	Test Method	MITSUBISHI ENGINEERING JAPAN/GS2010MKR
Compared to the anti leakage trace index	CTI	UL 746	PLC 4
impact performance	Test Condition	Test Method	MITSUBISHI ENGINEERING JAPAN/GS2010MKR
Impact strength of simply supported beam without notch	23°C	ISO 179	55 kJ/m²

Supplier Join

Get App

Top

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index