Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEI 9085 WH8E479 SABIC INNOVATIVE US
ULTEM™ 
Railway Applications、national defense、Profile、Aircraft interior parts
High mobility、Low toxicity、Low smoke
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE US/9085 WH8E479
Impact strength of cantilever beam gap23°CISO 180/1A13 kJ/m²
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/9085 WH8E479
Tensile modulusISO 527-2/13050 Mpa
tensile strength 断裂ISO 527-2/571.0 Mpa
elongation屈服ASTM D6387.0 %
Tensile strain屈服ISO 527-2/56.7 %
tensile strength 断裂ASTM D63874.0 Mpa
Flexural modulus50.0mm跨距ASTM D7902920 Mpa
tensile strength 屈服ISO 527-2/588.0 Mpa
Tensile modulusASTM D6383440 Mpa
elongation断裂ASTM D63872 %
bending strength屈服,50.0mm跨距ASTM D790138 Mpa
ISO 17890.0 Mpa
Flexural modulusISO 1782750 Mpa
Tensile strain断裂ISO 527-2/550 %
tensile strength 屈服ASTM D63884.0 Mpa
flammabilityTest ConditionTest MethodSABIC INNOVATIVE US/9085 WH8E479
FAAFlammabilityFAR25.853<5
OSU peak heat release rateFAR25.85336.0 kW/m²
VerticalBurnTest60s),passesat，TestaFAR25.8532.0 sec
OSU total heat releaseFAR25.85316.0 kW·min/m²
Limiting Oxygen IndexASTM D286349 %
physical property Test ConditionTest MethodSABIC INNOVATIVE US/9085 WH8E479
Shrinkage rateMD：3.20mm内部方法0.50-0.70 %
Melt volume flow rate360°C/5.0kgISO 113365.5 cm3/10min
Water absorption rate平衡,23°C,50%RHISO 620.17 %
饱和,23°CISO 620.39 %
melt mass-flow rate295°C/6.6kgASTM D12388.9 g/10min
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/9085 WH8E479
vicatISO 306/B120173 °C
Heat distortion temperature1.8MPa,Unannealed,64.0mmSpan，HDTISO 75-2/Af152 °C
1.8MPa,未退火,3.20mm，HDTASTM D648153 °C