HIPS H835 Hanong Chemical
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | Hanong Chemical/H835 |
|---|---|---|---|
| Water absorption rate | 24hr | ASTM D-570 | 0.050 % |
| melt mass-flow rate | 200℃,5kg | ASTM D-1238 | 4.5 g/10min |
| Mechanical properties | Test Condition | Test Method | Hanong Chemical/H835 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D-256 | 118 J/m | |
| Rockwell hardness | ASTM D-785 | 55 L scale | |
| bending strength | ASTM D-790 | 39.2 MPa | |
| elongation at break | ASTM D-638 | 60 % | |
| Flexural modulus | ASTM D-790 | 1770 MPa | |
| tensile strength | ASTM D-638 | 20.6 MPa |
| Electrical performance | Test Condition | Test Method | Hanong Chemical/H835 |
|---|---|---|---|
| dielectric constant | 1E+6Hz | ASTM D-150 | 2.500 |
| Volume resistivity | ASTM D-257 | 1E+17 ohm.cm |
| physical property | Test Condition | Test Method | Hanong Chemical/H835 |
|---|---|---|---|
| density | ASTM D-792 | 1.04 g/cm | |
| Shrinkage rate | Flow | ASTM D-955 | 0.40-0.70 % |
| Thermal performance | Test Condition | Test Method | Hanong Chemical/H835 |
|---|---|---|---|
| combustibility | 3.17mm,ALL | UL 94 | HB |
| Heat distortion temperature | 1.80MPa，未退火，6.40mm，HDT | ASTM D-648 | 75.0 ℃ |
| combustibility | 1.59mm,ALL | UL 94 | HB |
| vicat | Loading 2(50N) | ASTM D-1525 | 88.0 ℃ |
| Loading 1(10N) | ASTM D-1525 | 96.0 ℃ |