PA6 73G35HSL BK262 DUPONT SHENZHEN
Zytel®
Automotive components、Electronic and Electrical
lubrication、High temperature resistan、Filler: Glass fiber reinf、35% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | DUPONT SHENZHEN/73G35HSL BK262 |
|---|---|---|---|
| Linear thermal expansion coefficient | MD | ISO11359-2 | 2E-05 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO75-2/B | 220 °C |
| 1.8MPa,未退火 | ISO75-2/A | 208 °C | |
| Linear thermal expansion coefficient | TD | ISO11359-2 | 1.1E-04 cm/cm/°C |
| Melting Temperature | ISO11357-3 | 221 °C | |
| Vicat Softening Temperature | ISO306/B50 | 215 °C |
| Physical | Test Condition | Test Method | DUPONT SHENZHEN/73G35HSL BK262 |
|---|---|---|---|
| Moisture Absorption | 平衡,23°C,2.00mm,50%RH | ISO62 | 1.8 % |
| 饱和,23°C,2.00mm | ISO62 | 5.8 % | |
| Modeling Shrinkage | TD | ISO294-4 | 1.0 % |
| MD | ISO294-4 | 0.20 % |
| Mechanical Properties | Test Condition | Test Method | DUPONT SHENZHEN/73G35HSL BK262 |
|---|---|---|---|
| Flexural Modulus | ISO178 | 9900 Mpa | |
| Tensile Strain | 断裂 | ISO527-2 | 3.2 % |
| Tensile Stress | 断裂 | ISO527-2 | 190 Mpa |
| Flexural Stress | ISO178 | 280 Mpa | |
| Tensile Modulus | ISO527-2 | 11000 Mpa |
| Impact Properties | Test Condition | Test Method | DUPONT SHENZHEN/73G35HSL BK262 |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 90 kJ/m² |
| -30°C | ISO179/1eU | 90 kJ/m² | |
| Multi-Axial Instrumented Impact Energy | 23°C | ISO6603-2 | 3.00 J |
| Flammability | Test Condition | Test Method | DUPONT SHENZHEN/73G35HSL BK262 |
|---|---|---|---|
| Burning Rate | 1.00mm | ISO3795 | 24 mm/min |
| Flammability level | 1.5mm | IEC60695-11-10,-20 | HB |
| FMVSS Flammability | FMVSS302 | B | |
| Flame Rating | 1.5mm | UL94 | HB |