Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS 2130A1-HD9000 JAPAN POLYPLASTIC
DURAFIDE®
Industrial components,Automotive Applications,mechanical
Lubricity,Filler: Carbon fiber rein, power seeking,Lubricity,30%,Filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | JAPAN POLYPLASTIC/2130A1-HD9000 |
|---|---|---|---|
| melt viscosity | 310℃、1000/sec | ISO 11443 | 380 Pa·s |
| hardness | Test Condition | Test Method | JAPAN POLYPLASTIC/2130A1-HD9000 |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | 110 M（Scale） |
| Basic performance | Test Condition | Test Method | JAPAN POLYPLASTIC/2130A1-HD9000 |
|---|---|---|---|
| Water absorption rate | 23℃、水中24小时 | ISO 62 | 0.02 % |
| density | ISO 1183 | 1.44 g/cm |
| Mechanical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/2130A1-HD9000 |
|---|---|---|---|
| bending strength | 23°C | ISO 178 | 300 Mpa |
| ISO 178 | 300 Mpa | ||
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 5.5 kJ/m² |
| Flexural modulus | ISO 178 | 21200 Mpa | |
| 23°C | ISO 178 | 21200 Mpa | |
| Charpy Notched Impact Strength | ISO 179/1eA | 5.5 KJ/m | |
| elongation at break | 23°C | ISO 527-2 | 1.3 % |
| tensile strength | ISO 527-1 | 215 Mpa | |
| fracture strain | ISO 527-1 | 1.3 % | |
| tensile strength | 23°C | ISO 527-2 | 215 Mpa |
| Electrical performance | Test Condition | Test Method | JAPAN POLYPLASTIC/2130A1-HD9000 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 2000 Ω·cm | |
| Surface Resistivity | IEC 60093 | 200 Ω | |
| Volume resistivity | IEC 60093 | 2E+03 Ω.cm |
| Flame retardant performance | Test Condition | Test Method | JAPAN POLYPLASTIC/2130A1-HD9000 |
|---|---|---|---|
| UL flame retardant rating | UL -94 | V-0 0.75mm |
| physical property | Test Condition | Test Method | JAPAN POLYPLASTIC/2130A1-HD9000 |
|---|---|---|---|
| Shrinkage rate | 流动方向，80℃×2mmt | 0.1 % | |
| Water absorption rate | (23°C,24hr) | ISO 62 | 0.04 % |
| Shrinkage rate | 垂直方向，80℃×2mmt | 0.6 % |
| Thermal performance | Test Condition | Test Method | JAPAN POLYPLASTIC/2130A1-HD9000 |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/Af | 265 °C |
| 1.8MPa，HDT | ISO 75-1 | 265 °C | |
| Linear coefficient of thermal expansion | 流动方向 | ISO 11359-2 | 1 |
| MD | ISO 11359-2 | 1E-05 cm/cm/°C | |
| 垂直方向 | - | 4 | |
| TD | ISO 11359-2 | 4E-05 cm/cm/°C |