Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates

PPS 1130A1 JAPAN POLYPLASTIC
DURAFIDE®
Household appliances,Household appliances,Fitness equipment,Automotive sector,Bottle cap
high strength,High temperature resistan,High toughness,Flame retardant,enhance
UL
SGS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Supplementary Information | Test Condition | Test Method | JAPAN POLYPLASTIC/1130A1 |
---|---|---|---|
ColorNumber | HF2000/HD9050 |
hardness | Test Condition | Test Method | JAPAN POLYPLASTIC/1130A1 |
---|---|---|---|
Rockwell hardness | M级 | ISO 2039-2 | 105 |
Basic performance | Test Condition | Test Method | JAPAN POLYPLASTIC/1130A1 |
---|---|---|---|
Water absorption rate | 23℃,水中24小时 | ISO 62 | 0.01 % |
melt viscosity | 310℃,1000/sec | ISO 11443 | 350 Pa·s |
density | ISO 1183 | 1.57 g/cm³ |
Electrical performance | Test Condition | Test Method | JAPAN POLYPLASTIC/1130A1 |
---|---|---|---|
Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 4 | |
relative permittivity | 1kHz | IEC 60250 | 4.00 |
dielectric strength | 3.00mm | IEC 60243-1 | 16 KV/mm |
relative permittivity | 1MHz | IEC 60250 | 4.00 |
Volume resistivity | ASTM D257/IEC 60093 | 3.0 x 10^16 Ω.cm | |
IEC 60093 | 3×1016 Ω·cm | ||
Dissipation Factor | 1MHz | IEC 60250 | 2E-03 |
1kHz | IEC 60250 | 1E-03 | |
Dielectric loss | 3mmt | IEC 60243-1 | 16 KV/mm |
Dissipation Factor | 耐电弧性 | IEC 60250 | 124 sec |
Volume resistivity | IEC 60093 | 3E+16 ohms·cm | |
Surface Resistivity | IEC 60093 | 2×1017 Ω | |
Leakage Tracking Index (CTI) | IEC 60112 | 150 V |
Mechanical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/1130A1 |
---|---|---|---|
bending strength | ASTM D790/ISO 178 | 245 kg/cm²(MPa)[Lb/in²] | |
Charpy Notched Impact Strength | ISO 179/1eA | 10.0 kJ/m² | |
Flexural modulus | ASTM D790/ISO 178 | 10000 kg/cm²(MPa)[Lb/in²] | |
bending strength | ISO 178 | 245 Mpa | |
Tensile strain | 断裂 | ISO 527-2 | 2.0 % |
Flexural modulus | ISO 178 | 10000 Mpa | |
elongation at break | ASTM D638/ISO 527 | 2 % | |
tensile strength | ASTM D638/ISO 527 | 170 kg/cm²(MPa)[Lb/in²] | |
ISO 527-1 | 170 Mpa | ||
fracture strain | ISO 527-1 | 2 % | |
tensile strength | ISO 527-2 | 170 Mpa |
Physical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/1130A1 |
---|---|---|---|
density | ASTM D792/ISO 1183 | 1.57 | |
Water absorption rate | ASTM D570/ISO 62 | 0.01 % |
flammability | Test Condition | Test Method | JAPAN POLYPLASTIC/1130A1 |
---|---|---|---|
UL flame retardant rating | UL 94 | V-0 |
physical property | Test Condition | Test Method | JAPAN POLYPLASTIC/1130A1 |
---|---|---|---|
Shrinkage rate | 流动方向,80℃×2mmt | 0.3 % | |
垂直方向,80℃×2mmt | 0.6 % | ||
Water absorption rate | 23°C,24hr | ISO 62 | 0.030 % |
melt viscosity | 310°C,1000sec^-1 | ISO 11443 | 350000 mPa·s |
Thermal performance | Test Condition | Test Method | JAPAN POLYPLASTIC/1130A1 |
---|---|---|---|
Combustibility (rate) | UL 94 | V-0 | |
Linear coefficient of thermal expansion | 垂直方向 | 4 ×10-5/℃ | |
流动方向 | ISO 11359-2 | 2 ×10-5/℃ | |
TD | 内部方法 | 4E-05 cm/cm/°C | |
Heat distortion temperature | 1.8MPa,HDT | ISO 75-1 | 260 °C |
1.8MPa,未退火,HDT | ISO 75-2/A | 260 °C | |
Linear coefficient of thermal expansion | MD | 内部方法 | 2E-05 cm/cm/°C |
ASTM D696/ISO 11359 | - mm/mm.℃ |