ABS+PA Sicoblend N8065 Entec Polymers
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Entec Polymers/Sicoblend N8065 |
|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 18 kJ/m² |
| 23°C | ISO 180/1A | 70 kJ/m² | |
| 23°C1 | ISO 180/1A | 无断裂 |
| Mechanical properties | Test Condition | Test Method | Entec Polymers/Sicoblend N8065 |
|---|---|---|---|
| tensile strength | 断裂 | ISO 527-2 | 35.0 MPa |
| Tensile strain | 断裂 | ISO 527-2 | 100 % |
| tensile strength | 屈服 | ISO 527-2 | 40.0 MPa |
| Flexural modulus | ISO 178 | 1800 MPa | |
| bending strength | ISO 178 | 55.0 MPa |
| flammability | Test Condition | Test Method | Entec Polymers/Sicoblend N8065 |
|---|---|---|---|
| UL flame retardant rating | 3.2mm | 内部方法 | HB |
| 1.6mm | 内部方法 | HB |
| physical property | Test Condition | Test Method | Entec Polymers/Sicoblend N8065 |
|---|---|---|---|
| Shrinkage rate | ISO 2577 | 0.60to0.90 % | |
| melt mass-flow rate | 240°C/10.0kg | ISO 1133 | 24 g/10min |
| Water absorption rate | 23°C,24hr | ISO 62 | 1.4 % |
| density | ISO 1183 | 1.07 g/cm³ |
| Thermal performance | Test Condition | Test Method | Entec Polymers/Sicoblend N8065 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 65.0 °C |
| vicat | ISO 306/B50 | 103 °C | |
| melting temperature | ISO 3146 | 230 °C |