PA66 A3WG6-BK BASF MALAYSIA
Ultramid®
machine、Mechanical components、container、Profile、Automotive sector、Shell
High rigidity、Oil resistant、dimensional stability 、heat-resisting
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Mechanical properties | Test Condition | Test Method | BASF MALAYSIA/A3WG6-BK |
---|---|---|---|
tensile strength | 断裂, 23°C | ISO 527-2 | 179 Mpa |
Tensile strain | 断裂, 23°C | ISO 527-2 | 2.6 % |
Flexural modulus | 23°C | ISO 178 | 8730 Mpa |
flammability | Test Condition | Test Method | BASF MALAYSIA/A3WG6-BK |
---|---|---|---|
UL flame retardant rating | 0.71 mm | UL 94 | HB |
3.0 mm | UL 94 | HB | |
1.5 mm | UL 94 | HB |
physical property | Test Condition | Test Method | BASF MALAYSIA/A3WG6-BK |
---|---|---|---|
Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 1.7 % |
饱和, 23°C | ISO 62 | 5.5 % |
Thermal performance | Test Condition | Test Method | BASF MALAYSIA/A3WG6-BK |
---|---|---|---|
RTI | 3.0 mm | UL 746 | 130 °C |
RTI Elec | 3.0 mm | UL 746 | 125 °C |
0.71 mm | UL 746 | 125 °C | |
Heat distortion temperature | 1.8 MPa, 未退火,HDT | ISO 75-2/A | 250 °C |
RTI Imp | 1.5 mm | UL 746 | 115 °C |
3.0 mm | UL 746 | 120 °C | |
melting temperature | ISO 3146 | 260 °C | |
RTI Elec | 1.5 mm | UL 746 | 125 °C |
RTI | 1.5 mm | UL 746 | 115 °C |
injection | Test Condition | Test Method | BASF MALAYSIA/A3WG6-BK |
---|---|---|---|
drying time | 2.0 to 4.0 hr | ||
Suggested maximum moisture content | 0.15 % | ||
Injection Pressure | 3.50 to 12.5 Mpa | ||
Processing (melt) temperature | 280 to 305 °C | ||
drying temperature | 80 °C | ||
Temperature | 80 to 90 °C | ||
injection speed | 快速 |