PET 935 NC010 DUPONT USA
Rynite® 
Automotive Applications、household electrical appl
Glass fiber reinforced、High temperature resistan
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodDUPONT USA/935 NC010
Impact strength of simply supported beam without notch23°CISO 179/1eU25 kJ/m²
-30°CISO 179/1eU20 kJ/m²
hardnessTest ConditionTest MethodDUPONT USA/935 NC010
Rockwell hardnessR计秤ISO 2039-2115
M计秤ISO 2039-275
Electrical performanceTest ConditionTest MethodDUPONT USA/935 NC010
Compared to the Leakage Tracking Index (CTI)IEC 60112PLC 2
dielectric strengthIEC 60243-139 KV/mm
Volume resistivityIEC 600931E+15 ohms·cm
relative permittivity100HzIEC 602504.50
Dissipation Factor100HzIEC 602500.030
relative permittivity1MHzIEC 602504.10
Surface ResistivityIEC 600931E+14 ohms
Dissipation Factor1MHzIEC 602500.014
Mechanical propertiesTest ConditionTest MethodDUPONT USA/935 NC010
bending strengthASTM D790/ISO 178141 kg/cm²(MPa)[Lb/in²]
Tensile modulusISO 527-210200 Mpa
ASTM D412/ISO 52710200 kg/cm²(MPa)[Lb/in²]
Flexural modulusASTM D790/ISO 1789100 kg/cm²(MPa)[Lb/in²]
Suspended wall beam without notch impact strengthASTM D256425 J/m
bending strengthASTM D790141 Mpa
Tensile creep modulus1000hrISO 899-17690 Mpa
tensile strength 断裂ISO 527-285.0 Mpa
elongation at breakASTM D638/ISO 5272.0 %
Impact strength of cantilever beam gapASTM D25664 J/m
Rockwell hardnessASTM D78575
Flexural modulusASTM D7909600 Mpa
elongation at breakASTM D6382.0 %
tensile strength ASTM D63889.6 Mpa
Tensile modulusASTM D6389930 Mpa
Tensile creep modulus1hrISO 899-19350 Mpa
Tensile strain断裂ISO 527-22.0 %
Flexural modulusISO 1789100 Mpa
compressive strengthASTM D695141 Mpa
otherTest ConditionTest MethodDUPONT USA/935 NC010
characteristic刚性良好 抗老化性良好 抗弯曲
Color自然色
purpose电气/电子应用领域 汽车领域应用
Physical propertiesTest ConditionTest MethodDUPONT USA/935 NC010
densityASTM D792/ISO 11831.58
flammabilityTest ConditionTest MethodDUPONT USA/935 NC010
UL flame retardant rating0.75mmUL 94HB
0.75mmIEC 60695-11-10,-20HB
Fogging-G-valuecondensateISO 64521E-04 g
UL flame retardant rating1.5mmIEC 60695-11-10,-20HB
FMVSS flammabilityFMVSS302B
Limiting Oxygen IndexISO 4589-221 %
UL flame retardant rating1.5mmUL 94HB
burning rate1.00mmISO 3795<100 mm/min
processabilityTest ConditionTest MethodDUPONT USA/935 NC010
Melt Temperature280-300 %
physical property Test ConditionTest MethodDUPONT USA/935 NC010
Shrinkage rate3.20 mm，垂直ASTM D9550.0065 cm/cm
TDISO 294-40.70 %
MDISO 294-40.30 %
Water absorption rate饱和,23°C,2.00mmISO 620.83 %
MediumDensity1.32 g/cm³
Ejection Temperature170 °C
Shrinkage rate3.20 mm，平行流动ASTM D9550.0035 cm/cm
SpecificHeatCapacity of Melt1790 J/kg/°C
ThermalConductivityofMelt0.32 W/m/K
Melt volume flow rate280°C/5.0kgISO 11335.00 cm3/10min
Water absorption rate平衡,23°C,2.00mm,50%RHISO 620.13 %
Thermal performanceTest ConditionTest MethodDUPONT USA/935 NC010
vicatISO 306/B50205 °C
melting temperature252 °C
Linear coefficient of thermal expansionTD：EffectiveThermalDiffusivityISO 11359-21.4E-07 m²/s
Limiting Oxygen IndexASTM D2863-- %
melting temperatureISO 11357-3252 °C
Linear coefficient of thermal expansionTD：--ISO 11359-25.2E-05 cm/cm/°C
Heat distortion temperature66 psi， 未退火，HDTASTM D648241 °C
Linear coefficient of thermal expansionMD：-40to23°CISO 11359-22.6E-05 cm/cm/°C
TD：-40to23°CISO 11359-25.3E-05 cm/cm/°C
MD：--ISO 11359-21.6E-05 cm/cm/°C
Heat distortion temperature264 psi，未退火，HDTASTM D648215 °C
HDTASTM D648/ISO 75235 ℃（℉）
0.45MPa,未退火，HDTISO 75-2/B235 °C
1.8MPa,未退火，HDTISO 75-2/A200 °C
Linear coefficient of thermal expansionASTM E8310.000016 cm/cm/ ℃
UL flame retardant ratingUL 94HB