PA+PP Latiblend 5262 LATI S.p.A.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LATI S.p.A./Latiblend 5262 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 30 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| Supplementary Information | Test Condition | Test Method | LATI S.p.A./Latiblend 5262 |
|---|---|---|---|
| dimensional stability | 54.0 |
| Mechanical properties | Test Condition | Test Method | LATI S.p.A./Latiblend 5262 |
|---|---|---|---|
| tensile strength | 屈服,23°C | ISO 527-2/5 | 22.0 MPa |
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 150 % |
| tensile strength | 断裂,23°C | ISO 527-2/5 | 20.0 MPa |
| Tensile modulus | 23°C | ISO 527-2/1 | 750 MPa |
| Tensile strain | 屈服,23°C | ISO 527-2/5 | 6.0 % |
| physical property | Test Condition | Test Method | LATI S.p.A./Latiblend 5262 |
|---|---|---|---|
| Shrinkage rate | MD:2.00mm | ISO 294-4 | 1.3to1.7 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.20 % |
| density | ISO 1183 | 0.970 g/cm³ | |
| Shrinkage rate | TD:2.00mm | ISO 294-4 | 1.4to1.8 % |
| Thermal performance | Test Condition | Test Method | LATI S.p.A./Latiblend 5262 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 80.0 °C |
| vicat | ISO 306/B50 | 70.0 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 45.0 °C |
| Continuous use temperature | 70.0 °C | ||
| Linear coefficient of thermal expansion | MD：30到100°C | ISO 11359-2 | 4E-05 cm/cm/°C |