Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 K-FHG12 DSM HOLAND
Akulon®
--
Glass fiber reinforced,High mobility,Thermal stability,Filler: Glass fiber reinf,60% filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DSM HOLAND/K-FHG12 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 90 kJ/m² |
| -30°C | ISO 179/1eU | 85 kJ/m² |
| Mechanical properties | Test Condition | Test Method | DSM HOLAND/K-FHG12 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 20000 Mpa | |
| bending strength | ISO 178 | 365 Mpa | |
| Flexural modulus | ISO 178 | 19500 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 2.2 % |
| tensile strength | 断裂 | ISO 527-2 | 235 Mpa |
| flammability | Test Condition | Test Method | DSM HOLAND/K-FHG12 |
|---|---|---|---|
| Burning wire flammability index | 3.1mm | IEC 60695-2-12 | 850 °C |
| UL flame retardant rating | 1.6mm | IEC 60695-11-10,-20 | HB |
| physical property | Test Condition | Test Method | DSM HOLAND/K-FHG12 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 0.80 % |
| MD | ISO 294-4 | 0.20 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 1.0 % |
| 饱和,23°C | ISO 62 | 3.6 % |
| Thermal performance | Test Condition | Test Method | DSM HOLAND/K-FHG12 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 220 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 220 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 210 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1E-05 cm/cm/°C |
| TD | ISO 11359-2 | 4E-05 cm/cm/°C |