Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 2300GV1/10 CELANESE USA
CELANEX®
Electrical applications,Automotive Applications
High toughness,Hydrolysis resistance,Thermal stability,Weather resistance,UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | CELANESE USA/2300GV1/10 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 26 kJ/m² |
| -30°C | ISO 179/1eU | 26 kJ/m² |
| Electrical performance | Test Condition | Test Method | CELANESE USA/2300GV1/10 |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 28 KV/mm | |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 4.00 |
| Dissipation Factor | 100Hz | IEC 60250 | 1.3E-03 |
| relative permittivity | 1MHz | IEC 60250 | 3.90 |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.019 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| Mechanical properties | Test Condition | Test Method | CELANESE USA/2300GV1/10 |
|---|---|---|---|
| Tensile creep modulus | 1hr | ISO 899-1 | 4600 Mpa |
| Tensile modulus | ISO 527-2/1A/1 | 4700 Mpa | |
| bending strength | 23°C | ISO 178 | 130 Mpa |
| Tensile creep modulus | 1000hr | ISO 899-1 | 3500 Mpa |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 90.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 3.5 % |
| flammability | Test Condition | Test Method | CELANESE USA/2300GV1/10 |
|---|---|---|---|
| UL flame retardant rating | 1.2mm | UL 94 | HB |
| 1.5mm | UL 94 | HB | |
| Limiting Oxygen Index | ISO 4589-2 | 19 % |
| Filling analysis | Test Condition | Test Method | CELANESE USA/2300GV1/10 |
|---|---|---|---|
| DensityMelt | 内部方法 | 1.170 g/cm³ | |
| ThermalConductivityofMelt | 内部方法 | 0.14 W/m/K | |
| SpecificHeatCapacity of Melt | 内部方法 | 1870 J/kg/°C |
| physical property | Test Condition | Test Method | CELANESE USA/2300GV1/10 |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| Melt volume flow rate | 250°C/2.16kg | ISO 1133 | 21.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | CELANESE USA/2300GV1/10 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 225 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 210 °C |
| vicat | ISO 306/B50 | 205 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 190 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 6E-05 cm/cm/°C |
| Heat distortion temperature | 8.0MPa,未退火，HDT | ISO 75-2/C | 60.0 °C |