ABS/PBT KU2-7604 LANXESS GERMANY
Pocan®
Electrical and electronic
Low warpage、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LANXESS GERMANY/KU2-7604 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| 23°C | ISO 179/1eU | NoBreak | |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | NoBreak |
| -30°C | ISO 180/1U | NoBreak |
| Supplementary Information | Test Condition | Test Method | LANXESS GERMANY/KU2-7604 |
|---|---|---|---|
| ISO Shortcut | ISO 7792 | PBT+PC.GFHLMPR.11-020 |
| hardness | Test Condition | Test Method | LANXESS GERMANY/KU2-7604 |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 93.0 Mpa |
| Electrical performance | Test Condition | Test Method | LANXESS GERMANY/KU2-7604 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | V |
| Mechanical properties | Test Condition | Test Method | LANXESS GERMANY/KU2-7604 |
|---|---|---|---|
| Flexural modulus | 23°C | ISO 178/A | 2000 Mpa |
| Bending Strain | 23°C | ISO 178/A | 5.0 % |
| tensile strength | 屈服,23°C | ISO 527-2/50 | 45.0 Mpa |
| bending strength | 3.5%Strain,23°C | ISO 178/A | 65.0 Mpa |
| Tensile strain | 屈服,23°C | ISO 527-2/50 | 3.5 % |
| Tensile modulus | 23°C | ISO 527-2/1 | 2000 Mpa |
| Nominal tensile fracture strain | 23°C | ISO 527-2/50 | >20 % |
| bending strength | 23°C4 | ISO 178/A | 70.0 Mpa |
| flammability | Test Condition | Test Method | LANXESS GERMANY/KU2-7604 |
|---|---|---|---|
| Burning wire flammability index | 0.8mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 775 °C |
| 1.6mm | IEC 60695-2-13 | 775 °C | |
| UL flame retardant rating | 0.8mm | UL 94 | V-0 |
| Hot filament ignition temperature | 0.8mm | IEC 60695-2-13 | 775 °C |
| physical property | Test Condition | Test Method | LANXESS GERMANY/KU2-7604 |
|---|---|---|---|
| Shrinkage rate | MD:120°C,4小时,2.00mm3 | ISO 2577 | 0.80 % |
| Apparent density | ISO 60 | 0.80 g/cm³ | |
| Shrinkage rate | MD:250°C,2.00mm2 | ISO 2577 | 0.80 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.10 % |
| 饱和,23°C | ISO 62 | 0.30 % | |
| Shrinkage rate | TD:120°C,4小时,2.00mm3 | ISO 2577 | 0.80 % |
| Melt volume flow rate | 260°C/5.0kg | ISO 1133 | 20.0 cm3/10min |
| Shrinkage rate | TD:250°C,2.00mm2 | ISO 2577 | 0.80 % |
| Thermal performance | Test Condition | Test Method | LANXESS GERMANY/KU2-7604 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 225 °C | |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 1E-04 cm/cm/°C |
| vicat | ISO 306/B120 | 115 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 100 °C |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 75.0 °C |