Electrical performance	Test Condition	Test Method	LANXESS GERMANY/AKV30H2.0 NC
Dissipation factor	23°C,1MHz	IEC 60250	0.018
Volume resistivity	23°C	IEC 60093	1E+15 ohms·cm
Dielectric strength	23°C,1.00mm	IEC 60243-1	40 KV/mm
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 0
Surface resistivity		IEC 60093	1E+14 ohms
Relative permittivity	23°C,100Hz	IEC 60250	4.00
Dissipation factor	23°C,100Hz	IEC 60250	9E-03
Relative permittivity	23°C,1MHz	IEC 60250	4.00
mechanical properties	Test Condition	Test Method	LANXESS GERMANY/AKV30H2.0 NC
Tensile strain	Break,23°C	ISO 527-2/5	3.0 %
Bending modulus	23°C	ISO 178/A	8400 Mpa
Bending modulus		23°C	ASTM D790	841 Mpa
bending strength	23°C	ISO 178	290 Mpa
tensile strength	Break,23°C	ISO 527-2/5	185 Mpa
tensile strength		Break,23°C	ASTM D638	179 Mpa
Tensile modulus	23°C	ISO 527-2/1	10600 Mpa
bending strength	FlexuralStrainatFlexuralStrength5(23°C)		4.0 %
bending strength		23°C	ASTM D790	290 Mpa
elongation	Break,23°C	ASTM D638	3.0 %
bending strength	3.5%Strain	ISO 178/A	-- Mpa
Tensile modulus	23°C	ASTM D638	10300 Mpa
thermal performance	Test Condition	Test Method	LANXESS GERMANY/AKV30H2.0 NC
Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	1E-04 cm/cm/°C
Hot deformation temperature	8.0MPa,Unannealed	ISO 75-2/C	135 °C
Hot deformation temperature		0.45MPa,Unannealed	ISO 75-2/B	250 °C
Vicat softening temperature		ISO 306/B120	>230 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	250 °C
Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	2.5E-05 cm/cm/°C
Melting temperature		ISO 11357-3	263 °C
hardness	Test Condition	Test Method	LANXESS GERMANY/AKV30H2.0 NC
Ball Pressure Test		ISO 2039-1	230 Mpa
flammability	Test Condition	Test Method	LANXESS GERMANY/AKV30H2.0 NC
Extreme Oxygen Index		ISO 4589-2	23 %
UL flame retardant rating	3.2mm	UL 94	HB
Burning wire flammability index	2.0mm	IEC 60695-2-12	600 °C
UL flame retardant rating	1.6mm	UL 94	HB
Physical properties	Test Condition	Test Method	LANXESS GERMANY/AKV30H2.0 NC
Shrinkage rate	MD:280°C,3.00mm2	ISO 2577	0.35 %
		MD:120°C,2hr,3.00mm3	ISO 2577	0.040 %
		TD:280°C,3.00mm2	ISO 2577	1.5 %
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	2.0 %
Water absorption rate		Saturation,23°C	ISO 62	5.5 %
Shrinkage rate	TD:120°C,2hr,3.00mm3	ISO 294-4	0.050 %
Apparent density		ISO 60	0.70 g/cm³
impact performance	Test Condition	Test Method	LANXESS GERMANY/AKV30H2.0 NC
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	90 kJ/m²
Impact strength of simply supported beam without notch		-30°C	ISO 179/1eU	70 kJ/m²
Supplementary Information	Test Condition	Test Method	LANXESS GERMANY/AKV30H2.0 NC
ISO Shortcut		ISO 1874	PA66.GR.14-110.GF30