Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
AS(SAN) HD 20 INEOS STYRO THAILAND
Luran®
--
enhance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | INEOS STYRO THAILAND/HD 20 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179 | 16 kJ/m² |
| 23°C | ISO 179 | 16 kJ/m² |
| hardness | Test Condition | Test Method | INEOS STYRO THAILAND/HD 20 |
|---|---|---|---|
| Rockwell hardness | M级 | 83 | |
| ball-indentation hardness | ISO 2039-1 | 165 Mpa |
| Electrical performance | Test Condition | Test Method | INEOS STYRO THAILAND/HD 20 |
|---|---|---|---|
| dielectric constant | 100Hz | IEC 60250 | 3.00 |
| Volume resistivity | IEC 60093 | 1E+16 ohms·cm | |
| Dissipation Factor | 100Hz | IEC 60250 | 4E-03 |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 7E-03 |
| Mechanical properties | Test Condition | Test Method | INEOS STYRO THAILAND/HD 20 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 3700 Mpa | |
| Tensile creep modulus | 1hr | ISO 899-1 | 3500 Mpa |
| Tensile strain | 断裂,23°C | ISO 527-2 | 3.0 % |
| bending strength | ISO 178 | 120 Mpa | |
| tensile strength | 屈服,23°C | ISO 527-2 | 72.0 Mpa |
| Tensile creep modulus | 1000hr | ISO 899-1 | 2800 Mpa |
| optical performance | Test Condition | Test Method | INEOS STYRO THAILAND/HD 20 |
|---|---|---|---|
| transmissivity | 550nm | ASTM D1003 | >89.0 % |
| Haze ratio | ASTM D1003 | <1.0 % | |
| refractive index | ISO 489 | 1.569 |
| physical property | Test Condition | Test Method | INEOS STYRO THAILAND/HD 20 |
|---|---|---|---|
| Apparent density | 0.65 g/cm³ | ||
| Shrinkage rate | ISO 294-4 | 0.30-0.70 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 22.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | INEOS STYRO THAILAND/HD 20 |
|---|---|---|---|
| thermal conductivity | DIN 52612 | 0.17 W/m/K | |
| Heat distortion temperature | 1.8MPa,Annealed，HDT | ISO 75-2/A | 86.0 °C |
| vicat | ISO 306/B50 | 106 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 7E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,Annealed，HDT | ISO 75-2/B | 99.0 °C |