Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEEK 770CA20 JILIN JOINATURE
ZYPEEK®
Aerospace、Electrical field、Electronic field、Electric wire、Cable、Industrial machinery、Medical supplies、Nursing supplies
enhance、Moderate liquidity、standard、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | JILIN JOINATURE/770CA20 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179/1U | 45 kJ/m² | |
| Suspended wall beam without notch impact strength | ISO 180/U | 40 kJ/m² | |
| Charpy Notched Impact Strength | ISO 179-1eA | 7 kJ/m² | |
| Impact strength of cantilever beam gap | ISO 180/A | 8 kJ/m² |
| Mechanical properties | Test Condition | Test Method | JILIN JOINATURE/770CA20 |
|---|---|---|---|
| bending strength | 断裂，23℃ | ISO 178 | 310 Mpa |
| Flexural modulus | 23℃ | ISO 178 | 16000 Mpa |
| compressive strength | 23℃ | ISO 604 | - Mpa |
| tensile strength | 断裂，23℃ | ISO 527 | 210 Mpa |
| Shore hardness | 23℃ | ISO 868 | 86 D 级 |
| Tensile strain | 断裂，23℃ | ISO 527 | 2.1 % |
| Electrical performance | Test Condition | Test Method | JILIN JOINATURE/770CA20 |
|---|---|---|---|
| Volume resistivity | 23 ℃，1V | IEC 60093 | 10^7 ohms·cm |
| physical property | Test Condition | Test Method | JILIN JOINATURE/770CA20 |
|---|---|---|---|
| density | 结晶 | ISO 1183 | 1.37 g/cm³ |
| Shrinkage rate | TD | ISO 294-4 | 0.2 % |
| MD | ISO 294-4 | 0.7 % | |
| Water absorption rate | 23℃，24hr，3.2 mm厚拉伸棒 | ISO 62-1 | 0.05 % |
| melt mass-flow rate | 380℃，5.0kg | ISO 1133 | 4 g/10min |
| Water absorption rate | 平衡，23℃ | ISO 62-1 | 0.4 % |
| Thermal performance | Test Condition | Test Method | JILIN JOINATURE/770CA20 |
|---|---|---|---|
| Linear coefficient of thermal expansion | 低于Tg沿着流动方向 | ISO 11359 | 8 ppm/K |
| Heat distortion temperature | 1.8 Mpa，HDT | ISO 75-f | 325 °C |
| melting temperature | Tg（起始） | ISO 11357 | 143 °C |
| thermal conductivity | 23℃ | ISO 22007-4 | 0.95 W/m/K |
| Linear coefficient of thermal expansion | 高于Tg沿着流动方向 | ISO 11359 | 8 ppm/K |
| specific heat | 23℃ | DSC | 1.8 kJ/kg /℃ |