Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 5101G-15 TORAY JAPAN
Toraycon®
Automotive Applications,Electrical components
High impact resistance,Fast forming cycle
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TORAY JAPAN/5101G-15 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 60 kJ/m² |
| Supplementary Information | Test Condition | Test Method | TORAY JAPAN/5101G-15 |
|---|---|---|---|
| BarFlowLength | 250°C,1.00mm | 内部方法 | 8.50 CM |
| hardness | Test Condition | Test Method | TORAY JAPAN/5101G-15 |
|---|---|---|---|
| Rockwell hardness | M计秤,23°C | ISO 2039-2 | 64 |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/5101G-15 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 40 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 125 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 4700 kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 89 M | |
| coefficient of friction | 0.19 | ||
| Tensile modulus | 23°C | ISO 527-2 | 5000 Mpa |
| elongation at break | ASTM D638/ISO 527 | 5 % | |
| bending strength | 23℃ | ASTM D790 | 125 Mpa |
| Flexural modulus | 23℃ | ASTM D790 | 4.7 GPa |
| Rockwell hardness | ASTM D785 | M89 | |
| tensile strength | ASTM D638/ISO 527 | 95 kg/cm²(MPa)[Lb/in²] | |
| coefficient of friction | 对本身 | ASTM D1894 | 0.19 |
| Friction coefficient - vs. Metal | SuzukiMethod | 0.14 | |
| Tensile strain | 断裂,23°C | ISO 527-2 | 4.0 % |
| elongation | 23℃ | ASTM D638 | 5 % |
| bending strength | 23°C | ISO 178 | 145 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2 | 90.0 Mpa |
| Flexural modulus | 23°C | ISO 178 | 4700 Mpa |
| Impact strength of cantilever beam gap | 无缺口，-40℃ | ASTM D256 | 40 KJ/m |
| tensile strength | 23℃ | ASTM D638 | 95 Mpa |
| Impact strength of cantilever beam gap | 缺口，23℃ | ASTM D256 | 130 J/m |
| 缺口，-40℃ | ASTM D256 | 100 J/m | |
| coefficient of friction | 对金属 | ASTM D1894 | 0.14 |
| Impact strength of cantilever beam gap | 无缺口，23℃ | ASTM D256 | 60 KJ/m |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/5101G-15 |
|---|---|---|---|
| arc resistance | ASTM D495 | 110 S | |
| dielectric constant | 50Hz | ASTM D150 | 3.4 |
| Dielectric loss | 10，正切 | ASTM D150 | 0.02 |
| dielectric strength | ASTM D149 | 22 MV/m | |
| dielectric constant | ASTM D150/IEC 60250 | 3.4 | |
| Dielectric loss | 50Hz，正切 | ASTM D150 | 0.001 |
| Dissipation Factor | 23°C,50Hz | IEC 60250 | 1E-03 |
| Volume resistivity | ASTM D257/IEC 60093 | 2.0X10^14 Ω.cm | |
| Dissipation Factor | 23°C,1MHz | IEC 60250 | 0.020 |
| dielectric constant | 23°C,50Hz | IEC 60250 | 3.40 |
| 23°C,1kHz | IEC 60250 | 3.50 | |
| Volume resistivity | ASTM 257 | 2.0 | |
| dielectric strength | IEC 60243-1 | 22 KV/mm | |
| Volume resistivity | IEC 60093 | 4E+16 ohms·cm | |
| arc resistance | IEC 60950 | 110 sec | |
| dielectric constant | 10 | ASTM D150 | 3.5 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 0 |
| other | Test Condition | Test Method | TORAY JAPAN/5101G-15 |
|---|---|---|---|
| characteristic | 15%玻璃纤维增强级.高抗冲击级 |
| Physical properties | Test Condition | Test Method | TORAY JAPAN/5101G-15 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.36 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.07 % |
| flammability | Test Condition | Test Method | TORAY JAPAN/5101G-15 |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| physical property | Test Condition | Test Method | TORAY JAPAN/5101G-15 |
|---|---|---|---|
| Shrinkage rate | TD:3.00mm2 | 内部方法 | 1.5 % |
| MD:3.00mm4 | 内部方法 | 0.60 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.070 % |
| 23℃,24hr | ASTM D570 | 0.07 % |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/5101G-15 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| Heat distortion temperature | 0.45MPa，HDT | ASTM D648 | 220 °C |
| HDT | ASTM D648/ISO 75 | 204 ℃（℉） | |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 220 °C | |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 195 °C | |
| Linear coefficient of thermal expansion | MD：-30到100°C | ISO 11359-2 | 5.5E-05 cm/cm/°C |
| Heat distortion temperature | 1.82Mpa，HDT | ASTM D648 | 204 °C |
| Linear coefficient of thermal expansion | ASTM D696 | 5.5 | |
| ASTM D696/ISO 11359 | 5.5x10^-5 mm/mm.℃ | ||
| UL flame retardant rating | UL 94 | HB |