Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
HDPE MarFlex® 9608XD USA Chevron Phillips
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | USA Chevron Phillips/MarFlex® 9608XD |
|---|---|---|---|
| elongation | TD:断裂,32µm,挤塑薄膜 | ASTM D882 | 790 % |
| Secant modulus | 1%正割,TD:32µm,铸造薄膜 | ASTM D882 | 841 MPa |
| tensile strength | TD:断裂,32µm,挤塑薄膜 | ASTM D882 | 23.0 MPa |
| Elmendorf tear strength | MD:31.8µm | ASTM D1922 | 13.5 kN/m |
| tensile strength | MD:断裂,32µm,挤塑薄膜 | ASTM D882 | 29.0 MPa |
| Dart impact | 31.8µm，流延膜 | ASTM D1709 | 13.5 kN/m |
| Water Vapor Transmission Rate | 32µm,铸造薄膜 | ASTMF1249 | 5.0 g/m²/24hr |
| Elmendorf tear strength | TD:31.8µm | ASTM D1922 | 38.6 kN/m |
| elongation | MD:断裂,32µm,挤塑薄膜 | ASTM D882 | 870 % |
| Secant modulus | 1%正割,MD:32µm,铸造薄膜 | ASTM D882 | 758 MPa |
| optical performance | Test Condition | Test Method | USA Chevron Phillips/MarFlex® 9608XD |
|---|---|---|---|
| Haze ratio | 31.8µm,铸造薄膜 | ASTM D1003 | 11 % |
| gloss | 60°,31.8µm,铸造薄膜 | ASTM D2457 | 120 |
| physical property | Test Condition | Test Method | USA Chevron Phillips/MarFlex® 9608XD |
|---|---|---|---|
| density | ASTM D1505 | 0.962 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 8.0 g/10min |