Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 4701-7000 SABIC INNOVATIVE US
LEXAN™
Electronic and electrical
High temperature resistan、transparent
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/4701-7000 |
|---|---|---|---|
| Thermal Conductivity | ISO 8302 | 0.21 W/m/K | |
| Heat Deflection Temperature | 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 | ISO 75-2/Ae | 150 °C |
| Vicat Softening Temperature | -- | ISO 306/B50 | 175 °C |
| Ball PressureTest | 123 到 127°C | IEC 60695-10-2 | 通过 |
| Vicat Softening Temperature | -- | ISO 306/B120 | 170 °C |
| Heat Deflection Temperature | 0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 | ISO 75-2/Be | 165 °C |
| Vicat Softening Temperature | -- | ISO 306/A50 | 185 °C |
| Coefficient of Linear Thermal Expansion (Flow) | 23 到 80°C | ISO 11359-2 | 8.0E-5 cm/cm/°C |
| Hardness | Test Condition | Test Method | SABIC INNOVATIVE US/4701-7000 |
|---|---|---|---|
| Rockwell Hardness | R 计秤 | ISO 2039-2 | 127 |
| Injection | Test Condition | Test Method | SABIC INNOVATIVE US/4701-7000 |
|---|---|---|---|
| Middle Temperature | 310 到 330 °C | ||
| Processing (Melt) Temp | 325 到 360 °C | ||
| Drying Time | 3.0 到 4.0 hr | ||
| Rear Temperature | 300 到 320 °C | ||
| Nozzle Temperature | 320 到 340 °C | ||
| Drying Temperature | 125 到 135 °C | ||
| Front Temperature | 320 到 340 °C | ||
| Hopper Temperature | 60 到 80 °C | ||
| Mold Temperature | 100 到 125 °C |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/4701-7000 |
|---|---|---|---|
| Modeling Shrinkage - Flow | 内部方法 | 0.90 % | |
| Melt Volume flow Rate | 300°C/5.0 kg | ISO 1133 | 6.00 cm3/10min |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/4701-7000 |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | 2300 Mpa | |
| Tensile Strain | 断裂 | ISO 527-2/50 | > 50 % |
| 屈服 | ISO 527-2/50 | 7.0 % | |
| Flexural Modulus | ISO 178 | 2300 Mpa | |
| Tensile Stress | 屈服 | ISO 527-2/50 | 70.0 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/4701-7000 |
|---|---|---|---|
| Unnotched Izod Impact Strength | 23°C | ISO 180/1U | 无断裂 |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 13 kJ/m² |
| 23°C | ISO 179/1eA | 46 kJ/m² | |
| Notched Izod Impact Strength | 23°C | ISO 180/1A | 35 kJ/m² |
| -30°C | ISO 180/1A | 11 kJ/m² | |
| Charpy Unnotched Impact Strength | 23°C | ISO 179/1eU | 无断裂 |
| Unnotched Izod Impact Strength | -30°C | ISO 180/1U | 无断裂 |
| Charpy Unnotched Impact Strength | -30°C | ISO 179/1eU | 无断裂 |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/4701-7000 |
|---|---|---|---|
| Glow Wire Flammability Index | 2.0 mm | IEC 60695-2-12 | 850 °C |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/4701-7000 |
|---|---|---|---|
| Dissipation Factor? | 100 Hz | IEC 60250 | 0.026 |
| Relative Permittivity | 1 MHz | IEC 60250 | 3.10 |