Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA46 TW363 DSM HOLAND
Stanyl®
Casters、Automotive Applications
Thermal stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DSM HOLAND/TW363 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 75 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 26 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 80 kJ/m² |
| -40°C | ISO 180/1A | 40 kJ/m² |
| Mechanical properties | Test Condition | Test Method | DSM HOLAND/TW363 |
|---|---|---|---|
| Flexural modulus | 160°C | ISO 178 | 350 Mpa |
| Tensile modulus | -- | ISO 527-2 | 1850 Mpa |
| tensile strength | 屈服, 160°C | ISO 527-2 | 30.0 Mpa |
| 屈服, 120°C | ISO 527-2 | 35.0 Mpa | |
| Nominal tensile fracture strain | -- | ISO 527-2 | > 50 % |
| Flexural modulus | 120°C | ISO 178 | 400 Mpa |
| -- | ISO 178 | 1800 Mpa | |
| tensile strength | 屈服 | ISO 527-2 | 60.0 Mpa |
| Nominal tensile fracture strain | 120°C | ISO 527-2 | > 50 % |
| Tensile modulus | 160°C | ISO 527-2 | 350 Mpa |
| Nominal tensile fracture strain | 160°C | ISO 527-2 | > 50 % |
| Tensile modulus | 120°C | ISO 527-2 | 400 Mpa |
| Electrical performance | Test Condition | Test Method | DSM HOLAND/TW363 |
|---|---|---|---|
| relative permittivity | 100 Hz | IEC 60250 | 3.60 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 1 | |
| dielectric strength | IEC 60243-1 | 25 KV/mm | |
| Volume resistivity | IEC 60093 | 1.0E+15 ohms·cm | |
| relative permittivity | 1 MHz | IEC 60250 | 3.20 |
| physical property | Test Condition | Test Method | DSM HOLAND/TW363 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 3.0 % |
| density | ISO 1183 | 1.10 g/cm³ | |
| Shrinkage rate | 流量 | ISO 294-4 | 2.0 % |
| 横向流量 | ISO 294-4 | 2.0 % |
| Thermal performance | Test Condition | Test Method | DSM HOLAND/TW363 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 295 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 200 °C |
| 1.8 MPa, 未退火，HDT | ISO 75-2/A | 90.0 °C | |
| Thermal Index - 5000 hr | IEC 60216 | 135 °C | |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 1.6E-4 cm/cm/°C |
| 横向 | ISO 11359-2 | 1.8E-4 cm/cm/°C |