POM F10-03H KEP KOREA
KEPITAL®
Automotive sector、Electrical field、Electronic field、Industrial components、machine、Mechanical components
Fatigue resistance、Chemical resistance、Anti creep、Good liquidity、Good forming performance、Thermal stability、wear resistant、high viscosity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | KEP KOREA/F10-03H |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2800 Mpa | |
| bending strength | ISO 178 | 90.0 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 40 % |
| Flexural modulus | ISO 178 | 2650 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 12 % |
| tensile strength | ISO 527-2 | 68.0 Mpa |
| Electrical performance | Test Condition | Test Method | KEP KOREA/F10-03H |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 19 KV/mm | |
| Volume resistivity | IEC 60093 | 1E+14 ohms·cm | |
| Surface Resistivity | IEC 60093 | 1E+16 ohms |
| flammability | Test Condition | Test Method | KEP KOREA/F10-03H |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | KEP KOREA/F10-03H |
|---|---|---|---|
| Shrinkage rate | MD：3.00mm | 内部方法 | 2.2 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 3.0 g/10min |
| Thermal performance | Test Condition | Test Method | KEP KOREA/F10-03H |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 168 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 100 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.2E-04 cm/cm/°C |