Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC+Polyester XYLEX™ HX7509HP resin SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC/XYLEX™ HX7509HP resin |
|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C9 | ISO 180/1A | 8.0 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 10 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 70 J/m |
| 23°C | ASTM D256 | 850 J/m | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 77.0 J |
| Impact strength of cantilever beam gap | 23°C9 | ISO 180/1A | 9.0 kJ/m² |
| -10°C9 | ISO 180/1A | 6.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC/XYLEX™ HX7509HP resin |
|---|---|---|---|
| elongation | 断裂4 | ASTM D638 | 140 % |
| tensile strength | 屈服4 | ASTM D638 | 60.0 MPa |
| Flexural modulus | --6 | ISO 178 | 2260 MPa |
| elongation | 断裂 | ISO 527-2/50 | 130 % |
| Tensile modulus | -- | ISO 527-2/1 | 2300 MPa |
| bending strength | 屈服,50.0mm跨距5 | ASTM D790 | 95.0 MPa |
| tensile strength | 屈服 | ISO 527-2/50 | 60.0 MPa |
| bending strength | --6,7 | ISO 178 | 92.0 MPa |
| elongation | 屈服 | ISO 527-2/50 | 5.8 % |
| 屈服4 | ASTM D638 | 6.3 % | |
| Tensile modulus | --3 | ASTM D638 | 2150 MPa |
| tensile strength | 断裂4 | ASTM D638 | 63.0 MPa |
| 断裂 | ISO 527-2/50 | 62.0 MPa | |
| Flexural modulus | 50.0mm跨距5 | ASTM D790 | 2300 MPa |
| optical performance | Test Condition | Test Method | SABIC/XYLEX™ HX7509HP resin |
|---|---|---|---|
| Haze ratio | 2540µm | ASTM D1003 | 2.0 % |
| transmissivity | 2540µm | ASTM D1003 | 88.0 % |
| flammability | Test Condition | Test Method | SABIC/XYLEX™ HX7509HP resin |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | SABIC/XYLEX™ HX7509HP resin |
|---|---|---|---|
| density | ASTMD792 | 1.20 g/cm³ | |
| Shrinkage rate | MD:3.20mm | 内部方法 | 0.40to0.60 % |
| melt mass-flow rate | 265°C/2.16kg | ASTM D1238 | 12 g/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.050 % |
| 饱和,23°C | ISO 62 | 0.12 % | |
| Shrinkage rate | TD:3.20mm | 内部方法 | 0.50to0.70 % |
| Melt volume flow rate | 265°C/2.16kg | ISO 1133 | 11.5 cm³/10min |
| Thermal performance | Test Condition | Test Method | SABIC/XYLEX™ HX7509HP resin |
|---|---|---|---|
| thermal conductivity | ISO 8302 | 0.23 W/m/K | |
| Linear coefficient of thermal expansion | MD:-40到40°C | ISO 11359-2 | 6.8E-05 cm/cm/°C |
| TD:-40到40°C | ASTME831 | 1E-04 cm/cm/°C | |
| vicat | -- | ISO 306/B50 | 125 °C |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 119 °C |
| vicat | -- | ASTMD152511 | 126 °C |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 106 °C |
| 1.8MPa,未退火,64.0mm跨距10，HDT | ISO 75-2/Af | 108 °C | |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 1E-04 cm/cm/°C |
| TD:-40到40°C | ISO 11359-2 | 6.8E-05 cm/cm/°C |