PK SCHULAKETON CF 20 A SCHULMAN USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | A SCHULMAN USA/SCHULAKETON CF 20 |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 8.0 kJ/m² |
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 45 kJ/m² |
Charpy Notched Impact Strength | -40°C | ISO 179/1eA | 4.0 kJ/m² |
Impact strength of simply supported beam without notch | -40°C | ISO 179 | 33 kJ/m² |
Mechanical properties | Test Condition | Test Method | A SCHULMAN USA/SCHULAKETON CF 20 |
---|---|---|---|
Tensile strain | 屈服 | ISO 527-2/1A/50 | 17 % |
Tensile modulus | ISO 527-2/1A/1 | 12900 MPa | |
Flexural modulus | ISO 178 | 11900 MPa | |
tensile strength | 屈服 | ISO 527-2/1A/50 | 135 MPa |
flammability | Test Condition | Test Method | A SCHULMAN USA/SCHULAKETON CF 20 |
---|---|---|---|
UL flame retardant rating | 1.6mm | IEC 60695-11-10,-20 | HB |
3.2mm | IEC 60695-11-10,-20 | HB | |
3.2mm | UL 94 | HB | |
burning rate | ISO 3795 | <100 mm/min | |
UL flame retardant rating | 1.6mm | UL 94 | HB |
physical property | Test Condition | Test Method | A SCHULMAN USA/SCHULAKETON CF 20 |
---|---|---|---|
Melt volume flow rate | 240°C/2.16kg | ISO 1133 | 7.00 cm³/10min |
density | ISO 1183/A | 1.32 g/cm³ |
Thermal performance | Test Condition | Test Method | A SCHULMAN USA/SCHULAKETON CF 20 |
---|---|---|---|
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/Af | 210 °C |
vicat | ISO 306/B50 | 203 °C |