Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPA/F/PTFE UFL36SXQ BK1A959 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Car hood、Plastic bag、bearing、Electrical appliances
Thermal stability、wear resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/UFL36SXQ BK1A959 |
|---|---|---|---|
| NotchedIzodImpactStrength7 | 23°C | ISO180/1A | 9.1 kJ/m² |
| UnnotchedIzodImpactStrength7 | 23°C | ISO180/1U | 47 kJ/m² |
| Multi axis Instrumented Impact Energy | ISO6603-2 | 2.00 J | |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 8.90 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/UFL36SXQ BK1A959 |
|---|---|---|---|
| Tensile stress | 断裂 | ISO527-2/5 | 192 Mpa |
| elongation | 断裂 | ASTMD638 | 1.7 % |
| Bending modulus 6 | ISO178 | 11300 Mpa | |
| Flexural Strength5 | Break,50.0mmSpan | ASTMD790 | 233 Mpa |
| Tensile modulus | --3 | ASTMD638 | 15400 Mpa |
| Tensile strain | 断裂 | ISO527-2/5 | 2.0 % |
| Tensile strength 4 | Break | ASTMD638 | 189 Mpa |
| Flexural Strength5 | Yield,50.0mmSpan | ASTMD790 | 242 Mpa |
| Tensile modulus | --2 | ASTMD638 | 15400 Mpa |
| Dynamic | ASTMD3702Modified | 0.48 | |
| Static | ASTMD3702Modified | 0.52 | |
| Tensile stress | 屈服 | ISO527-2/5 | 192 Mpa |
| elongation | 屈服 | ASTMD638 | 1.8 % |
| Tensile modulus | ISO527-2/1 | 12600 Mpa | |
| Tensile strain | 屈服 | ISO527-2/5 | 2.0 % |
| Wear factor | Ring | ASTMD3702Modified | 0.100 10^-10in^5-min/ft-lb-hr |
| Flexural modulus | 50.0mmSpan | ASTMD790 | 10600 Mpa |
| Tensile strength 4 | 屈服 | ASTMD638 | 189 Mpa |
| Wear factor | Washer | ASTMD3702Modified | 5.00 10^-10in^5-min/ft-lb-hr |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/UFL36SXQ BK1A959 |
|---|---|---|---|
| Shrinkage rate | TD：24hr | ASTMD955 | 0.80to1.0 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 0.25 % |
| 24hr,50%RH | ASTMD570 | 0.15 % | |
| Shrinkage rate | MD：24小时 | ASTMD955 | 0.20to0.40 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/UFL36SXQ BK1A959 |
|---|---|---|---|
| 1.8MPa,未退火,3.20mm | ASTMD648 | 277 °C | |
| MD：-30到30°C | ASTMD696 | 2.1E-05 cm/cm/°C | |
| TD：-30to30°C | ASTMD696 | 4.5E-05 cm/cm/°C | |
| 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 273 °C |