| Thermal Properties | Test Condition | Test Method | DUPONT USA/HTR8206 |
|---|---|---|---|
| Melting Temperature | ISO11357-3 | 200 °C | |
| Effective Thermal Diffusivity | 5.44E-08 m²/s |
| Hardness | Test Condition | Test Method | DUPONT USA/HTR8206 |
|---|---|---|---|
| Shore Hardness | 邵氏D,15秒 | ISO868 | 38 |
| 邵氏D | ISO868 | 40 |
| Physical | Test Condition | Test Method | DUPONT USA/HTR8206 |
|---|---|---|---|
| Moisture Absorption | 平衡,23°C,2.00mm,50%RH | ISO62 | 1.3 % |
| 2100 J/kg/°C | |||
| MediumDensity | 1.02 g/cm³ | ||
| Melt Volume flow Rate | 220°C/2.16kg | ISO1133 | 14.0 cm3/10min |
| Modeling Shrinkage | TD | ISO294-4 | 1.5 % |
| 0.16 W/m/K | |||
| Modeling Shrinkage | MD | ISO294-4 | 1.4 % |
| Moisture Absorption | 23°C,24hr | ISO62 | 35 % |
| Mechanical Properties | Test Condition | Test Method | DUPONT USA/HTR8206 |
|---|---|---|---|
| Flexural Modulus | ISO178 | 80.0 Mpa | |
| Tensile Stress | 10%应变 | ISO527-2 | 5.40 Mpa |
| 5.0%应变 | ISO527-2 | 3.40 Mpa | |
| Tensile Strain | 断裂 | ISO527-2 | >300 % |
| Nominal Tensile Strain at Break | ISO527-2 | 420 % | |
| Tensile Stress | 断裂 | ISO527-2 | 20.0 Mpa |
| Tensile Modulus | ISO527-2 | 80.0 Mpa | |
| Tensile Stress | 50%应变 | ISO527-2 | 9.50 Mpa |
| Impact Properties | Test Condition | Test Method | DUPONT USA/HTR8206 |
|---|---|---|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | NoBreak |
| 23°C | ISO179/1eU | NoBreak |
| Flammability | Test Condition | Test Method | DUPONT USA/HTR8206 |
|---|---|---|---|
| Burning Rate | 1.00mm | ISO3795 | <100 mm/min |
| FMVSS Flammability | FMVSS302 | B |