PLA Futerro® Extrusion Futerro
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Futerro/Futerro® Extrusion |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO 180 | 3.5 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Futerro/Futerro® Extrusion |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 3500 MPa | |
| tensile strength | 断裂 | ISO 527-2 | 55.0 MPa |
| Tensile strain | 断裂 | ISO 527-2 | 6.0 % |
| tensile strength | 屈服 | ISO 527-2 | 60.0 MPa |
| bending strength | ISO 178 | 90.0 MPa |
| optical performance | Test Condition | Test Method | Futerro/Futerro® Extrusion |
|---|---|---|---|
| transmissivity | 2000µm | ISO 14782 | >90.0 % |
| Haze ratio | 2000µm | ISO 14782 | <5.0 % |
| Filling analysis | Test Condition | Test Method | Futerro/Futerro® Extrusion |
|---|---|---|---|
| Melt density | 230°C | 1.08to1.12 g/cm³ |
| physical property | Test Condition | Test Method | Futerro/Futerro® Extrusion |
|---|---|---|---|
| density | 25°C | ISO 1183 | 1.24 g/cm³ |
| melt mass-flow rate | 含水量 | ISO 1133 | <250 ppm |
| 210°C/2.16kg | ISO 1133 | 5.0to7.0 g/10min | |
| L-poly-LactideContent | ISO 1133 | >99 % | |
| FreeLactideContent | ISO 1133 | <0.40 % | |
| 190°C/2.16kg | ISO 1133 | 2.0to4.0 g/10min |
| Thermal performance | Test Condition | Test Method | Futerro/Futerro® Extrusion |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 145to175 °C | |
| Glass Transition Temperature | ISO 11357-2 | 52.0to60.0 °C |