Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PET X8300 SABIC INNOVATIVE US
XYLEX™
Electronic field、Electrical field
UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/X8300 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 10 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 95.0 J |
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 73 J/m |
| 23°C | ASTM D256 | 1100 J/m | |
| -30°C | ISO 180/1A | 7.0 kJ/m² | |
| -10°C | ISO 180/1A | 5.0 kJ/m² | |
| 23°C | ISO 180/1A | 8.0 kJ/m² |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/X8300 |
|---|---|---|---|
| Shore hardness | 邵氏D,10秒 | ASTM D2240 | 74 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/X8300 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 1600 Mpa | |
| elongation | 屈服 | ASTM D638 | 5.0 % |
| tensile strength | 断裂 | ASTM D638 | 46.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2/50 | >5.0 % |
| tensile strength | 断裂 | ISO 527-2/50 | 54.0 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 1680 Mpa |
| Tensile modulus | ASTM D638 | 1520 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 55.0 Mpa |
| elongation | 断裂 | ASTM D638 | 150 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 71.0 Mpa |
| ISO 178 | 78.0 Mpa | ||
| Flexural modulus | ISO 178 | 1700 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 47.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2/50 | >200 % |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/X8300 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | >1.0E+15 ohms·cm | |
| Surface Resistivity | ASTM D257 | >1.0E+15 ohms | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 0 |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE US/X8300 |
|---|---|---|---|
| Haze ratio | 2540µm | ASTM D1003 | 1.0 % |
| refractive index | ISO 489 | 1.539 | |
| transmissivity | 2540µm | ASTM D1003 | 88.0 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/X8300 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | V-2 |
| Burning wire flammability index | 1.0mm | IEC 60695-2-12 | 750 °C |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/X8300 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.80 % |
| TD：3.20mm | 内部方法 | 0.40-0.60 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| melt mass-flow rate | 265°C/2.16kg | ASTM D1238 | 15 g/10min |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.050 % |
| density | ASTM D792 | 1.20 g/cm³ | |
| ISO 1183 | 1.17 g/cm³ | ||
| Melt volume flow rate | 265°C/2.16kg | ISO 1133 | 15.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/X8300 |
|---|---|---|---|
| ball-indentation hardness | 85°C | IEC 60695-10-2 | Pass |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 1.1E-04 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 79.0 °C |
| vicat | ASTM D152511 | 91.0 °C | |
| Heat distortion temperature | 1.8MPa,未退火,100mm跨距9，HDT | ISO 75-2/Ae | 80.0 °C |
| 1.8MPa,未退火,64.0mm跨距10，HDT | ISO 75-2/Af | 78.0 °C | |
| Linear coefficient of thermal expansion | MD：23to60°C | ISO 11359-2 | 9E-05 cm/cm/°C |
| thermal conductivity | ISO 8302 | 0.23 W/m/K | |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 1.1E-04 cm/cm/°C |
| vicat | ISO 306/B120 | 96.0 °C | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| TD：-40to40°C | ISO 11359-2 | 1.1E-04 cm/cm/°C | |
| TD：23to60°C | ISO 11359-2 | 9E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 75.0 °C |