PA6 73G50HSLA BK416 DUPONT USA
Zytel®
Electronic and Electrical、Wear resistant accessorie、household electrical appl
High gloss、lubrication、Good appearance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/73G50HSLA BK416 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 100 kJ/m² |
| -30°C | ISO 179/1eU | 100 kJ/m² |
| Electrical performance | Test Condition | Test Method | DUPONT USA/73G50HSLA BK416 |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | -- ohms | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/73G50HSLA BK416 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 15500 Mpa | |
| Tensile creep modulus | 1hr | ISO 899-1 | -- Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 2.2 % |
| Flexural modulus | ISO 178 | 14300 Mpa | |
| Tensile creep modulus | 1000hr | ISO 899-1 | -- Mpa |
| tensile strength | 断裂 | ISO 527-2 | 233 Mpa |
| flammability | Test Condition | Test Method | DUPONT USA/73G50HSLA BK416 |
|---|---|---|---|
| FMVSS flammability | FMVSS302 | B | |
| Flammability level | 1.5mm | IEC 60695-11-10,-20 | HB |
| burning rate | 1.00mm | ISO 3795 | 31 mm/min |
| physical property | Test Condition | Test Method | DUPONT USA/73G50HSLA BK416 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 0.60 % |
| MD | ISO 294-4 | 0.30 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 4.5 % |
| MediumDensity | 1.24 g/cm³ | ||
| SpecificHeatCapacity of Melt | 2050 J/kg/°C | ||
| ThermalConductivityofMelt | 0.26 W/m/K | ||
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 1.5 % |
| Thermal performance | Test Condition | Test Method | DUPONT USA/73G50HSLA BK416 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 219 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 219 °C |
| vicat | ISO 306/B50 | 215 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 212 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.5E-05 cm/cm/°C |
| TD | ISO 11359-2 | 1E-04 cm/cm/°C |