PPO FE1520PW-801 SABIC INNOVATIVE NETHERLANDS
NORYL™
valve、Faucet、Water pump impeller、shower head
Low water absorption、Hot water resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/FE1520PW-801 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 23 kJ/m² |
| 23°C | ISO 180/1U | 25 kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 4.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 30 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 6.0 kJ/m² |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/FE1520PW-801 |
|---|---|---|---|
| ball-indentation hardness | H358/30 | ISO 2039-1 | 220 Mpa |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/FE1520PW-801 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 7180 Mpa | |
| ASTM D638 | 7110 Mpa | ||
| tensile strength | 断裂 | ISO 527-2/5 | 119 Mpa |
| elongation | 断裂 | ASTM D638 | 2.6 % |
| bending strength | ISO 178 | 165 Mpa | |
| Flexural modulus | ISO 178 | 6040 Mpa | |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | 内部方法 | 65.0 mg |
| Tensile strain | 断裂 | ISO 527-2/5 | 2.6 % |
| tensile strength | 断裂 | ASTM D638 | 119 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 6970 Mpa |
| bending strength | 断裂,50.0mm跨距 | ASTM D790 | 175 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/FE1520PW-801 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.20-0.40 % |
| TD：3.20mm | 内部方法 | 0.30-0.60 % | |
| Water absorption rate | 平衡,50%RH | ASTM D570 | 0.060 % |
| 饱和,23°C | ISO 62 | 0.20 % | |
| Melt volume flow rate | 280°C/10.0kg | ISO 1133 | 22.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/FE1520PW-801 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,Unannealed,100mmSpan，HDT | ISO 75-2/Be | 139 °C |
| vicat | -- | ISO 306/B120 | 144 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ISO 11359-2 | 7E-05 cm/cm/°C |
| vicat | -- | ISO 306/A50 | 150 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ISO 11359-2 | 3E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,Unannealed,100mmSpan，HDT | ISO 75-2/Ae | 132 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 135 °C |