Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS 900 TORAY JAPAN
Toyolac®
Washing machine
Carbon fiber reinforced、transparent
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TORAY JAPAN/900 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 12 kJ/m² |
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 160 J/m |
| 23°C,12.7mm | ASTM D256 | 140 J/m |
| hardness | Test Condition | Test Method | TORAY JAPAN/900 |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | ASTM D785 | 108 |
| R计秤,23°C | ISO 2039-2 | 108 |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/900 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 40 % |
| Tensile strain | 断裂,23°C | ISO 527-2 | 15 % |
| bending strength | 23°C | ISO 178 | 66.0 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2 | 48.0 Mpa |
| bending strength | ASTM D790 | 63.0 Mpa | |
| Flexural modulus | 23°C | ISO 178 | 1870 Mpa |
| ASTM D790 | 1810 Mpa | ||
| tensile strength | ASTM D638 | 41.0 Mpa |
| optical performance | Test Condition | Test Method | TORAY JAPAN/900 |
|---|---|---|---|
| Haze ratio | 3000µm | ISO 14782 | 2.0 % |
| transmissivity | 总计,3000µm | ISO 13468 | 86.0 % |
| flammability | Test Condition | Test Method | TORAY JAPAN/900 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | TORAY JAPAN/900 |
|---|---|---|---|
| density | 23°C | ISO 1183 | 1.08 g/cm³ |
| Shrinkage rate | 内部方法 | 0.40-0.60 % | |
| density | ASTM D792 | 1.08 g/cm³ | |
| melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 18 g/10min |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/900 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 81.0 °C |
| vicat | 90.0 °C | ||
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 76.0 °C |