Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS PC-510 TAIWAN CHIMEI
WONDERLOY®
Electronic and electrical
High mobility、Flame retardant、heat-resisting
MSDS
RoHS
UL
TDS
TDS
UL
MSDS
RoHS
SVHC
Processing
物质宣告书
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/ABS/TAIWAN CHIMEI/PC-510
SpiralFlow3.
内部方法
CM
4
density
ASTMD792
g/cm³
1
density
23°C
ISO1183
g/cm³
1
Melt Volume-Flow Rate (MVR)
260°C/2.16kg
ISO1133
cm3/10min
2
Melt mass flow rate
260°C/2.16kg
ASTMD1238
g/10min
2
Shrinkage rate
MD
ASTMD955
%
0
Shrinkage rate
ISO2577
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/ABS/TAIWAN CHIMEI/PC-510
FlexuralStrength
23°C
ASTMD790
Mpa
7
Impact strength of simply supported beam gap
-30°C
ISO179
kJ/m²
1
Impact strength of simply supported beam gap
23°C
ISO179
kJ/m²
4
Tensile strength
Yield,23°C
ASTMD638
Mpa
4
tensile strength
屈服
ISO527-2/50
Mpa
5
tensile strength
断裂
ISO527-2/50
Mpa
4
Tensile strain
Break,23°C
ASTMD638
%
1
elongation
断裂
ISO527-2/50
%
1
Bending modulus
23°C
ASTMD790
Mpa
2
Bending modulus
ISO178
Mpa
2
Bending stress
ISO178
Mpa
8
Suspended wall beam gap impact strength
23°C
ISO180
kJ/m²
4
Impact strength of cantilever beam gap
23°C,3.18mm
ASTMD256
J/m
5
Suspended wall beam gap impact strength
-30°C
ISO180
kJ/m²
1
Thermal performance
Test Condition
Test Method
Unit
PC/ABS/TAIWAN CHIMEI/PC-510
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
7
Hot deformation temperature
1.8MPa,未退火,6.40mm
ASTMD648
°C
8
Hot deformation temperature
1.8MPa,Unannealed,4.00mm
ISO75-2/A
°C
7
vicat softening point
--
ASTMD152510
°C
9
vicat softening point
--
ASTMD152511
°C
8
vicat softening point
--
ISO306/A50
°C
9
vicat softening point
--
ISO306/B50
°C
8
Linear coefficient of thermal expansion
MD：23到55°C
ISO11359-2
cm/cm/°C
8
Electrical performance
Test Condition
Test Method
Unit
PC/ABS/TAIWAN CHIMEI/PC-510
Surface resistivity
IEC60093
ohms
2
Volume resistivity
IEC60093
ohms·cm
3