Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC HF1130R SABIC INNOVATIVE US
LEXAN™
Automotive sector、Thin walled components
heat-resisting、Dimensional stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/HF1130R |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D1822 | 378 kJ/m² | |
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 54.2 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/HF1130R |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2370 Mpa | |
| elongation | 断裂 | ASTM D638 | 110 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 93.1 Mpa |
| elongation | 屈服 | ASTM D638 | 6.0 % |
| tensile strength | 断裂 | ASTM D638 | 65.5 Mpa |
| 屈服 | ASTM D638 | 62.1 Mpa | |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2310 Mpa |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE US/HF1130R |
|---|---|---|---|
| Haze ratio | 2540µm | ASTM D1003 | 1.0 % |
| transmissivity | 2540µm | ASTM D1003 | 88.0 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/HF1130R |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 25 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/HF1130R |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 127 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 6.8E-05 cm/cm/°C |
| MD：-40到40°C | ASTME831 | 7E-05 cm/cm/°C |