Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 5710G30-S2-BK MITSUBISHI ENGINEERING JAPAN
NOVADURAN™
Vehicle electronics,Fitness equipment,Bottle cap
Glass fiber reinforced,Flame retardant,Filler: Glass fiber reinf,30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5710G30-S2-BK |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 52 kJ/m² |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5710G30-S2-BK |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 10500 Mpa | |
| bending strength | ISO 178 | 190 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 2.0 % |
| Flexural modulus | ISO 178 | 9000 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 130 Mpa |
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5710G30-S2-BK |
|---|---|---|---|
| dielectric strength | 1.00mm | IEC 60243-1 | 28 KV/mm |
| Volume resistivity | IEC 60093 | 9E+16 ohms·cm | |
| dielectric strength | 2.00mm | IEC 60243-1 | 24 KV/mm |
| relative permittivity | 1MHz | IEC 60250 | 3.40 |
| Surface Resistivity | IEC 60093 | 5E+15 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.020 |
| physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5710G30-S2-BK |
|---|---|---|---|
| Shrinkage rate | MD:2.00mm | 0.40 % | |
| TD:2.00mm | 0.80 % | ||
| 吸水率(饱和,23°C) | 0.070 % |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5710G30-S2-BK |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 224 °C | |
| Linear coefficient of thermal expansion | MD：-30to120°C | ISO 11359-2 | 1E-05 cm/cm/°C |
| MD：50to120°C | ISO 11359-2 | 1E-05 cm/cm/°C | |
| TD：-30to120°C | ISO 11359-2 | 1E-04 cm/cm/°C | |
| MD：-30to50°C | ISO 11359-2 | 1E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 220 °C |
| Linear coefficient of thermal expansion | TD：-30to50°C | ISO 11359-2 | 7E-05 cm/cm/°C |
| TD：50to120°C | ISO 11359-2 | 1.2E-04 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 194 °C |