Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 8253HS BK102 BASF GERMANY
Ultramid®
Helmet、Automotive Applications、Engine parts
Thermal stability、high strength、Oil resistant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF GERMANY/8253HS BK102 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | NoBreak |
| Dart impact | 23°C | 内部方法 | 271 J |
| hardness | Test Condition | Test Method | BASF GERMANY/8253HS BK102 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 82 |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/8253HS BK102 |
|---|---|---|---|
| bending strength | 23°C | ISO 178 | 65.0 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2 | 60.0 Mpa |
| Tensile strain | 屈服,23°C | ISO 527-2 | 4.0 % |
| Flexural modulus | 23°C | ISO 178 | 1900 Mpa |
| bending strength | 23°C | ASTM D790 | 85.0 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 2400 Mpa |
| elongation | 屈服,23°C | ASTM D638 | 4.0 % |
| tensile strength | 屈服,23°C | ASTM D638 | 65.0 Mpa |
| Nominal tensile fracture strain | 23°C | ISO 527-2 | 40 % |
| Flexural modulus | 23°C | ASTM D790 | 2270 Mpa |
| elongation | 断裂,23°C | ASTM D638 | >100 % |
| flammability | Test Condition | Test Method | BASF GERMANY/8253HS BK102 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| 3.0mm | UL 94 | HB | |
| 6.0mm | UL 94 | HB | |
| 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | BASF GERMANY/8253HS BK102 |
|---|---|---|---|
| Shrinkage rate | MD：3.18mm | 1.2 % | |
| Water absorption rate | 饱和 | ASTM D570 | 8.1 % |
| 24hr | ASTM D570 | 1.5 % | |
| 23°C,24hr | ISO 62 | 1.5 % | |
| 平衡,50%RH | ASTM D570 | 2.3 % | |
| 平衡,23°C,50%RH | ISO 62 | 2.3 % | |
| 饱和,23°C | ISO 62 | 8.1 % |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/8253HS BK102 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 60.0 °C |
| RTI Elec | 6.0mm | UL 746 | 105 °C |
| RTI Str | 0.75mm | UL 746 | 95.0 °C |
| RTI Imp | 1.5mm | UL 746 | 105 °C |
| RTI Str | 6.0mm | UL 746 | 105 °C |
| melting temperature | ASTM D3418 | 220 °C | |
| RTI Elec | 0.71mm | UL 746 | 105 °C |
| 3.0mm | UL 746 | 105 °C | |
| RTI Imp | 3.0mm | UL 746 | 105 °C |
| melting temperature | ISO 3146 | 220 °C | |
| RTI Elec | 0.75mm | UL 746 | 105 °C |
| RTI Imp | 0.75mm | UL 746 | 95.0 °C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 160 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 55.0 °C | |
| RTI Str | 1.5mm | UL 746 | 105 °C |
| 3.0mm | UL 746 | 105 °C | |
| RTI Elec | 1.5mm | UL 746 | 105 °C |
| Linear coefficient of thermal expansion | MD | ASTME831 | 9.9E-05 cm/cm/°C |
| RTI Imp | 6.0mm | UL 746 | 105 °C |
| RTI Str | 0.71mm | UL 746 | 95.0 °C |
| RTI Imp | 0.71mm | UL 746 | 95.0 °C |