Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 1300-30 LG CHEM KOREA
LUPOY®
Lighting applications,Electrical applications
high strength,High rigidity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LG CHEM KOREA/1300-30 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 700 J/m |
| Mechanical properties | Test Condition | Test Method | LG CHEM KOREA/1300-30 |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2340 Mpa | |
| elongation | 断裂 | ASTM D638 | 150 % |
| 屈服 | ASTM D638 | 6.0 % | |
| bending strength | ASTM D790 | 96.0 Mpa | |
| tensile strength | 屈服,23°C | ASTM D638 | 60.0 Mpa |
| Flexural modulus | ASTM D790 | 2410 Mpa | |
| tensile strength | 极限 | ASTM D638 | 61.0 Mpa |
| Electrical performance | Test Condition | Test Method | LG CHEM KOREA/1300-30 |
|---|---|---|---|
| Dissipation Factor | 60Hz | ASTM D150 | 1E-03 |
| dielectric constant | 60Hz | ASTM D150 | 3.00 |
| Volume resistivity | 23°C | ASTM D257 | 2E+17 ohms·cm |
| dielectric strength | ASTM D149 | 17 KV/mm | |
| Compared to the Leakage Tracking Index (CTI) | 2.00mm | IEC 60112 | PLC 2 |
| optical performance | Test Condition | Test Method | LG CHEM KOREA/1300-30 |
|---|---|---|---|
| transmissivity | ASTM D1003 | 89.0 % | |
| refractive index | ASTM D542 | 1.586 | |
| Haze ratio | ASTM D1003 | 0.70to1.5 % |
| flammability | Test Condition | Test Method | LG CHEM KOREA/1300-30 |
|---|---|---|---|
| UL flame retardant rating | 2.5mm | UL 94 | V-2 |
| 3.0mm | UL 94 | V-2 | |
| GWIT | 2.0mm | IEC 60695-2-13 | 850 °C |
| Average degree of combustion | ASTM D635 | 3 CM | |
| UL flame retardant rating | 1.6mm | UL 94 | V-2 |
| Limiting Oxygen Index | ASTM D2863 | 26 % | |
| UL flame retardant rating | 0.50mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | LG CHEM KOREA/1300-30 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.50-0.70 % |
| Water absorption rate | 平衡,23°C,50%RH | ASTM D570 | 0.32 % |
| 23°C,24hr | ASTM D570 | 0.15 % | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 30 g/10min |
| Thermal performance | Test Condition | Test Method | LG CHEM KOREA/1300-30 |
|---|---|---|---|
| vicat | ASTM D15254 | 144 °C | |
| Ball pressure temperature | IEC 60598-1 | >125 °C | |
| Heat distortion temperature | 1.8MPa,Unannealed,4.00mm，HDT | ASTM D648 | 122 °C |
| 1.8MPa,Annealed,4.00mm，HDT | ASTM D648 | 136 °C | |
| Linear coefficient of thermal expansion | MD：-40到82°C | ASTM D696 | 6.8E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,Annealed,4.00mm，HDT | ASTM D648 | 139 °C |