PC/ABS T88GF-10 HI 901510 COVESTRO SHANGHAI
Bayblend®
Automotive Applications、Electrical applications、household electrical appl
heat-resisting、Flame retardant、Filler: Glass fiber reinf、10% filler by weight、10% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | COVESTRO SHANGHAI/T88GF-10 HI 901510 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180 | 35 kJ/m² |
| -30°C | ISO 180 | 35 kJ/m² | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/A | 8.0 kJ/m² |
| -30°C | ISO 180/A | 6.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | COVESTRO SHANGHAI/T88GF-10 HI 901510 |
|---|---|---|---|
| dielectric strength | 23°C,1.00mm | IEC 60243-1 | 35 KV/mm |
| relative permittivity | 23°C,1MHz | IEC 60250 | 3.00 |
| Volume resistivity | 23°C | IEC 60093 | 1E+16 ohms·cm |
| relative permittivity | 23°C,100Hz | IEC 60250 | 3.20 |
| Surface Resistivity | IEC 60093 | 1E+16 ohms | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 3 |
| Dissipation Factor | 23°C,100Hz | IEC 60250 | 2.5E-03 |
| 23°C,1MHz | IEC 60250 | 9E-03 |
| Mechanical properties | Test Condition | Test Method | COVESTRO SHANGHAI/T88GF-10 HI 901510 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 3.7 % |
| tensile strength | 断裂,23°C | ISO 527-2/5 | 95.0 Mpa |
| Tensile modulus | 23°C | ISO 527-2/1 | 4800 Mpa |
| Tensile strain | 屈服,23°C | ISO 527-2/5 | 3.2 % |
| tensile strength | 屈服,23°C | ISO 527-2/5 | 100 Mpa |
| flammability | Test Condition | Test Method | COVESTRO SHANGHAI/T88GF-10 HI 901510 |
|---|---|---|---|
| UL flame retardant rating | 0.9mm | UL 94 | HB |
| physical property | Test Condition | Test Method | COVESTRO SHANGHAI/T88GF-10 HI 901510 |
|---|---|---|---|
| density | 23°C | ISO 1183 | 1.22 g/cm³ |
| MeltViscosity | 260°C | ISO 11443-A | 205 Pa·s |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| 饱和,23°C | ISO 62 | 0.40 % | |
| Shrinkage rate | MD:260°C,3.00mm | ISO 2577 | 0.25-0.45 % |
| TD:260°C,3.00mm | ISO 2577 | 0.35-0.55 % |
| Thermal performance | Test Condition | Test Method | COVESTRO SHANGHAI/T88GF-10 HI 901510 |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 134 °C |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 4E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 133 °C |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO 11359-2 | 6.7E-05 cm/cm/°C |
| vicat | -- | ISO 306/B50 | 132 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 121 °C |