ABS PA-718 TAIWAN CHIMEI
POLYLAC®
small home appliances、Electronic field、Electrical field
High impact resistance、High gloss
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | TAIWAN CHIMEI/PA-718 |
|---|---|---|---|
| melt mass-flow rate | ASTM D-1238 | 1.6 g/10min |
| Mechanical properties | Test Condition | Test Method | TAIWAN CHIMEI/PA-718 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 720(10200) kg/cm²(MPa)[Lb/in²] | |
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 12(2.2) kg·cm/cm(J/M)ft·lb/in | |
| bending strength | 1/4＂ 2.8mm/min | ASTM D-790 | 720(10200) kg/cm2(lb/in2) |
| Impact strength of cantilever beam gap | 1/8 ＂23℃ | ASTM D-256 | 12(2.2) kg·cm/cm(ft-lb/in) |
| tensile strength | 1/8＂ 6mm/min | ASTM D-638 | 480(6800) kg/cm2(lb/in2) |
| Flexural modulus | ASTM D790/ISO 178 | 25000(350000) kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 30 % | |
| Shore hardness | 1/2＂ | ASTM D-785 | 114 R scale |
| Flexural modulus | 1/4＂ 2.8mm/min | ASTM D-790 | 25000(350000) kg/cm2(lb/in2) |
| elongation | 1/8＂ 6mm/min | ASTM D-638 | 30 % |
| Impact strength of cantilever beam gap | 1/4＂ 23℃ | ASTM D-256 | 10(1.8) kg·cm/cm(ft-lb/in) |
| tensile strength | ASTM D638/ISO 527 | 480(6800) kg/cm²(MPa)[Lb/in²] |
| other | Test Condition | Test Method | TAIWAN CHIMEI/PA-718 |
|---|---|---|---|
| characteristic | 注塑、高光泽、高硬度ABS.钢琴拷漆 | ||
| purpose | 电视机外框等 |
| Physical properties | Test Condition | Test Method | TAIWAN CHIMEI/PA-718 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.125 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 1.6 g/10min |
| Thermal performance | Test Condition | Test Method | TAIWAN CHIMEI/PA-718 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | 1/16＂HB | |
| Heat distortion temperature | 1/4＂，120℃/hr，HDT | ASTM D-648 | 86(186) ℃（℉） |
| HDT | ASTM D648/ISO 75 | 86(186) ℃（℉） | |
| vicat | ASTM D1525/ISO R306 | 103(217) ℃（℉） | |
| burning rate | UL -94 | 1/16＂HB | |
| vicat | 1/8＂，50℃/hr | ASTM D-1525 | 103(217) ℃（℉） |
| Hardness | Load 765g | ASTM D-3363 | H+ |