Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6T A350 MITSUI CHEM JAPAN
ARLEN™
Automotive sector、Shell
Glass fiber reinforced、Chemical resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | MITSUI CHEM JAPAN/A350 |
|---|---|---|---|
| Glass Fiber Content | 50 % |
| Basic performance | Test Condition | Test Method | MITSUI CHEM JAPAN/A350 |
|---|---|---|---|
| Water absorption rate | 23℃ | ASTM D-570 | 0.2 % |
| Mechanical properties | Test Condition | Test Method | MITSUI CHEM JAPAN/A350 |
|---|---|---|---|
| elongation | dry(moist) | ASTM D-638 | 3(3) % |
| Flexural modulus | dry(moist) | ASTM D-790 | 17000(15000) Mpa |
| Rockwell hardness | ASTM D-785 | 110 M Scale | |
| tensile strength | dry(moist) | ASTM D-638 | 300(270) Mpa |
| Impact strength of cantilever beam gap | dry(moist) | ASTM D-256 | 150(160) J/m |
| bending strength | dry(moist) | ASTM D-790 | 430(390) Mpa |
| Electrical performance | Test Condition | Test Method | MITSUI CHEM JAPAN/A350 |
|---|---|---|---|
| dielectric strength | dry | ASTM D-149 | 29 KV/mm |
| Dissipation Factor | 10 | ASTM D-150 | 0.018 |
| Volume resistivity | dry | ASTM D-257 | 10 Ω.cm |
| dielectric constant | 10 | ASTM D-150 | 4.5 |
| physical property | Test Condition | Test Method | MITSUI CHEM JAPAN/A350 |
|---|---|---|---|
| Shrinkage rate | 2mmt | ASTM D-955 | 0.2 % |
| Thermal performance | Test Condition | Test Method | MITSUI CHEM JAPAN/A350 |
|---|---|---|---|
| Heat distortion temperature | HDT | ASTM D-648 | 310 °C |
| melting temperature | 320 °C | ||
| Linear coefficient of thermal expansion | ASTM D-696 | 1.8 | |
| Glass transition temperature (Tg) | 125 °C | ||
| UL flame retardant rating | UL 94 | HB |